求翻译：In this pattern, the (300) reflection of β-form crystals is clearly seen at 2θ of about 16°, and the intensity of the β peak is even greater than that any of the α-characteristic peaks. This assuredly indicates the presence of β-form crystals in the samples containing the β-nucleating agent. Figure 3 shows the crystall是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
In this pattern, the (300) reflection of β-form crystals is clearly seen at 2θ of about 16°, and the intensity of the β peak is even greater than that any of the α-characteristic peaks. This assuredly indicates the presence of β-form crystals in the samples containing the β-nucleating agent. Figure 3 shows the crystall
问题补充： |
|
2013-05-23 12:21:38
在这个模式中，β-型结晶的（300）反射是清楚地看到在约16°2θ，和β峰的强度比任何的α-特征峰更大。这确实表明β型结晶的含有β-成核剂的样品中的存在。图3示出β型结晶的含有不同浓度的β-成核剂结晶在静态状态下134℃的样品中的结晶度。从图3中可以看出，有小的成核效率，如果上瘾小于0.05％，但含有的β-成核剂的迅速增加，直至剂含量的样品的β-型结晶度为0.1％以上，然后与不断提高剂含量略有增加。较高的成核剂浓度，较高的β-型结晶性变。这一结果清楚地表明，在这项工作中所用的添加剂对IPP一个突出的β-成核的效果。
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
在这个样式， β形式 (水晶的) 300反射大约清楚地看在16° 2θ，并且其中任一个α典型峰顶β峰顶的强度甚而大于。 这确定地在包含β-nucleating的代理的样品表明β形式水晶出现。 图3在包含β-nucleating的代理的不同的集中的样品显示β形式水晶结晶性被结晶在134 °C在静态状态之下。 从图3，它能被看见有一点nucleating的效率，如果致瘾少于0.05%是，但是迅速地包含β-nucleating的代理增量的样品的β形式结晶性，直到代理内容是超过0.1%轻微地然后增加与连续更高的代理内容。 越高nucleating的代理集中是，越高β形式结晶性变得。 这个结果清楚地表明
|
|
2013-05-23 12:26:38
在此模式中，β-窗体晶体 (300) 反射清楚地看到在约 16 °，2θ 和 β 峰的强度是甚至大于任何 α-特征峰。肯定地说，这表明 β-窗体晶体中含有 β 成核剂的样品的存在。图 3 显示了含有不同浓度的 β 成核剂结晶在静态状态下的 134 ° C 的样品中的 β-窗体晶体的结晶度。从图 3 可以看出是小成核效率是否上瘾小于 0.05%，但 β-窗体结晶度的样品含有 β 成核剂迅速增加直到代理内容是超过 0.1%，然后略有增加不断含量较高代理。成核剂浓度越高，越高 β-窗体结晶成为。这一结果清楚地表明这项工作中使用的添加剂有对 iPP β 成核效果显著。
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区