求翻译：1. The β-phase crystallinity of PP0 and PP1 increases rapidly until the shear rate reaches 20 s-1 and then decreases slightly with the shear rate increasing continuously. The formation mechanism of β crystals is shear-induced crystallization. The amount of β crystals is related to the amount of oriented α crystals form是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
1. The β-phase crystallinity of PP0 and PP1 increases rapidly until the shear rate reaches 20 s-1 and then decreases slightly with the shear rate increasing continuously. The formation mechanism of β crystals is shear-induced crystallization. The amount of β crystals is related to the amount of oriented α crystals form
问题补充： |
|
2013-05-23 12:21:38
1。 PP0和PP1增加的β-相结晶性迅速，直至剪切率达到20秒-1，然后与剪切速率连续增加稍有降低。 β晶体的形成机理是剪切诱导结晶。 β晶体的量与形成在不同的剪切速率下定向α晶体的量。该PP1的β-相结晶度比PP0较低的原因是，分散添加剂抑制取向α晶核的形成，然后导致诱导的β-相结晶度降低。
|
|
2013-05-23 12:23:18
1. PP0和PP1增量β阶段结晶性直到剪率迅速地到达20 s-1有一点然后减少与连续地增加剪的率。β水晶形成机制是剪诱发的结晶。相当数量β水晶与相当数量针对的α水晶有关被形成以不同的剪率。
|
|
2013-05-23 12:24:58
1. PP0和PP1增量β阶段结晶性直到剪率迅速地到达20 s-1轻微地然后减少以剪率连续增加。 β水晶形成机制是剪导致的结晶。 相当数量β水晶与相当数量针对的α水晶有关被形成以不同的剪率。 原因PP1 β阶段结晶性比那低PP0是被分散的添加剂克制针对的α中坚力量的形成然后造成导致的β阶段结晶性减少。
|
|
2013-05-23 12:26:38
1.Β-阶段结晶度的 PP0 和 PP1 迅速增加，直到剪切速率达到 20 s 1，然后减少略与剪切速率不断增加。Β 晶体的形成机制是剪切诱导结晶。Β 晶体的量是金额相关的面向的 α 晶体形成了不同的剪切率。Β 相结晶度 PP1 是比 PP0 低的原因是分散的添加剂克制面向的 α 核的形成，并且然后导致致的 β 相结晶度降低。
|
|