求翻译:The much larger ionic size of Ca2+(1.00 Å) compared to Ti4+ (0.605 Å) results in a lower Ti solid solution limit of x = 0.04 for Ba(Ti1xCax)O3x with DPT at TC = 44 C, and the sintering temperature had to be elevated to a higher temperature of 1500 C [9].是什么意思?

待解决 悬赏分:1 - 离问题结束还有
The much larger ionic size of Ca2+(1.00 Å) compared to Ti4+ (0.605 Å) results in a lower Ti solid solution limit of x = 0.04 for Ba(Ti1xCax)O3x with DPT at TC = 44 C, and the sintering temperature had to be elevated to a higher temperature of 1500 C [9].
问题补充:

  • 匿名
2013-05-23 12:21:38
正在翻译,请等待...
  • 匿名
2013-05-23 12:23:18
正在翻译,请等待...
  • 匿名
2013-05-23 12:24:58
Ca2+ 1.00 Å的更大的离子(大小) 与Ti4+ (0.605 Å) 结果比较在一个更低的钛固定解决方案极限x =  0.04为Ba( Ti1  xCax) O3  x与DPT在TC = 44  C和焊接温度必须被举起到一个更高的温度1500年 C (9)。
  • 匿名
2013-05-23 12:26:38
多离子大小的增加 Ca2 + (1.00 Å) 相比,钛 4 + (0.605 Å) 结果在 Ti 固溶体的下限 x = 0.04 为广管局 (Ti1 xCax) O3 用 DPT 在 TC 的 x = 44 C 和烧结温度了要提升到较高温度的 1500 C [9]。
  • 匿名
2013-05-23 12:28:18
大得多的离子大小的Ca2+[1]”相比,TI4+[0.605Å̊]结果TI在一个较低的可靠解决方案限制X=0.04BA[TI1xcax]O3X与部门在Tc=44C,和烧结温度已提升到一个更高的温度下的1500C[9]。
 
 
网站首页

湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区

 
关 闭