求翻译：Fig.3shows the HRC hardness at different Tempering temperatures.The hardness increased With increasing temperature until.The initial at 500 ℃ Hardness of T1and T2is 29HRC and 33HRC respectively After tempering at different temperatures for 3h, the hardness (HRC) of the two kinds of samples Can increase T2show the simil是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Fig.3shows the HRC hardness at different Tempering temperatures.The hardness increased With increasing temperature until.The initial at 500 ℃ Hardness of T1and T2is 29HRC and 33HRC respectively After tempering at different temperatures for 3h, the hardness (HRC) of the two kinds of samples Can increase T2show the simil
问题补充： |
|
2013-05-23 12:21:38
正在翻译，请等待...
|
|
2013-05-23 12:23:18
Fig.3shows在不同的回火温度的HRC坚硬。坚硬增加随着温度的增加直到。在T1and分别在磨炼的T2is 29HRC和33HRC的500 ℃坚硬的最初在3h的不同的温度以后，坚硬(HRC)这两样品可能增加T2show相似的26.T1and坚硬变异。当回火温度是大约600 ℃时，坚硬减少的Strongly.The高峰坚硬(HRC) T1and T2是37and 35respectively
|
|
2013-05-23 12:24:58
Fig.3shows HRC坚硬在不同的回火温度。坚硬增加随着温度的增加直到。最初在T1and T2is 29HRC和33HRC的500 ℃坚硬分别在磨炼在不同的温度以后为3h，这二 (的) 坚硬HRC样品可能增加T2show相似的26.T1and坚硬变异。当回火温度是大约600 ℃时， T1and T2的坚硬减少的Strongly.The (高峰) 坚硬HRC是37and 35respectively
|
|
2013-05-23 12:26:38
Fig.3shows HRC 硬度不同钢化温度。硬度增加，直到温度的增加。最初在 500 ℃ 硬度的 T1and T2is 29HRC 和 33HRC 分别为 3 h，硬度 (HRC) 的样本的两种不同温度下回火后可以增加 T2show 类似 26.T1and 硬度的变异。当回火温度是大约 600 ℃ 时，硬度下降 T1and T2 是 37and 35respectively 的 Strongly.The 峰值的硬度 (HRC)
|
|