求翻译：When the crystallization time reaches 10 h, the sample shows weak peaks associated with MFI structure in XRD pattern (Figure 2B-c), an obvious band (374 cm−1) assigned to 5-membered ring of Si-OSi and sharp bands (e.g., 307 and 1037 cm−1) attributed to TPA+ in the UV-Raman spectrum (Figure 2C-c) appear, suggesting that是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
When the crystallization time reaches 10 h, the sample shows weak peaks associated with MFI structure in XRD pattern (Figure 2B-c), an obvious band (374 cm−1) assigned to 5-membered ring of Si-OSi and sharp bands (e.g., 307 and 1037 cm−1) attributed to TPA+ in the UV-Raman spectrum (Figure 2C-c) appear, suggesting that
问题补充： |
|
2013-05-23 12:21:38
正在翻译，请等待...
|
|
2013-05-23 12:23:18
当结晶时间到达10 h时，样品在XRD样式(图2B-c)，一条明显的带显示微弱的峰顶与MFI结构相关(374 cm−1)分配了到Si OSi 5 membered圆环，并且锋利的带(即， 307和1037 cm−1)归因于在紫外喇曼光谱(图2C-c)的TPA+出现，建议少量的S SiZSM 5水晶被形成。
|
|
2013-05-23 12:24:58
当结晶时间到达10 h时，样品在XRD样式形象2B-c，一条明显的带374 (cm−1显示)微弱的峰顶与 (MFI结构相关) 被分配到5-membered SiOSi圆环，并且锋利的带 (即， 307和1037 cm−1) 归因于TPA+在紫外喇曼光谱 (形象2C-c) 看来，建议小量的SSiZSM 5水晶被形成。
|
|
2013-05-23 12:26:38
当结晶时间达到 10 h，该示例演示与 XRD 模式 (图 2B-c) 中的多边投资框架结构关联的弱峰时，明显乐队 (374 cm − 1) 分配给 5 元环的 Si OSi 和锋利乐队 (例如，307 和 1037 cm − 1） 归因于 TPA + 紫外拉曼光谱 （图 2 C-c） 中出现，暗示了少量的 S-Si-分子筛-5 晶体的形成。
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区