求翻译：ABSTRACT: The aim of this paper is to assess the performance of self-compacting glass concrete (SCGC) after exposure to four elevated temperatures of 300°C, 500°C, 600°C and 800°C. The influence of curing conditions on the high temperature performance of SCGC was also investigated. For each curing regime, five SCGC mix是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
ABSTRACT: The aim of this paper is to assess the performance of self-compacting glass concrete (SCGC) after exposure to four elevated temperatures of 300°C, 500°C, 600°C and 800°C. The influence of curing conditions on the high temperature performance of SCGC was also investigated. For each curing regime, five SCGC mix
问题补充： |
|
2013-05-23 12:21:38
摘要：本文的目的是接触到四个高温300℃ ， 500℃ ， 600 ℃和800℃后，以评估自密实混凝土玻璃（深圳创新投）的表现
|
|
2013-05-23 12:23:18
摘要：本文的目标将估计表现自变紧密的玻璃混凝土(SCGC)在对四高温的暴露以后300°C、500°C、600°C和800°C。治疗情况的影响对SCGC高温表现也被调查了。对于每个治疗的政权，五个SCGC混合物准备了与用于替换自然细颗粒聚合体在0%， 25%， 50%， 75%和100%的水平的被回收的玻璃(RG)。
|
|
2013-05-23 12:24:58
摘要： 本文的目标将在对四高温的暴露以后估计 (自已变紧密的) 玻璃混凝土SCGC表现300°C、500°C、600°C和800°C。 治疗情况的影响对SCGC高温度表现也被调查了。 为每个治疗的政权，五个SCGC混合物准备了与 (用于) 替换自然细颗粒聚合体在0%， 25%， 50%， 75%和100%的水平的被回收的玻璃RG。 在对高温的暴露以后，具体许多损失、密度、水多孔性、超音波脉冲速度 (UPV) 和水sorptivity是坚定的一个耐压强度测试然后进行了。 测试结果表明不管曝光温度，所有水被治疗的标本有更高的残余的强度和许多损失，当水多孔性和水sorptivity价值是低与对应的空
|
|
2013-05-23 12:26:38
摘要： 本文的目的是评估玻璃性能的自密实混凝土 (创新) 后四升高温度 300 ° C、 500 ° C、 600 ° C 和 800 ° c。对创新的耐高温性能的固化条件影响也进行了调查。为每个固化制度，五个创新混合物都精心准备了再生玻璃 (RG) 被用来取代天然细骨料一级的 0%、 25%、 50%、 75%和 100%。后接触到温度升高、 混凝土的质量损失、 密度、 水孔隙度，超声波脉冲速度 (UPV) 和水 sorptivity 被确定，然后进行抗压强度测试了。测试结果表明无论暴露温度，所有的水治愈标本有较高的残余强度和大规模损失虽然水孔隙率和水 sorptivity 值较低而相应空气
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区