求翻译：Fig. 3B shows the morphology of the formed PEDOT shell on the surface of PVC nanofibers, which was uniform and exhibited a typical fold shape due to the nature of EDOT chemical polymerization. The thickness of the PEDOT shell on PVC-310, PVC-650 and PVC1100 were 56 7 nm, 45 5 nm and 22 4 nm, respectively, measure是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Fig. 3B shows the morphology of the formed PEDOT shell on the surface of PVC nanofibers, which was uniform and exhibited a typical fold shape due to the nature of EDOT chemical polymerization. The thickness of the PEDOT shell on PVC-310, PVC-650 and PVC1100 were 56 7 nm, 45 5 nm and 22 4 nm, respectively, measure
问题补充： |
|
2013-05-23 12:21:38
图。
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
。 3B在PVC nanofibers表面显示被形成的PEDOT壳的形态学，是一致的并且陈列典型的折叠形状由于EDOT化学制品聚化的本质。 PEDOT壳的厚度在PVC-310， PVC-650和PVC1100分别为56 7毫微米， 45 5毫微米和22 4毫微米，计量从PEDOT管的TEM图象溶化得到的PVC核心与四氢呋喃。
|
|
2013-05-23 12:26:38
图 3B 显示形态的建制 pedot 膜壳表面的 PVC 纳米纤维，这是统一和展出一个典型折叠形状由于 EDOT 化学聚合的性质。Pedot 膜外壳上 PVC-310，厚度 PVC 650 和 PVC1100 分别为 56 7 毫微米、 45 5 毫微米和 22 4 毫微米，，从获得的溶解与四氢呋喃的 PVC 核心的 pedot 膜管的透射电镜图像测量。
|
|
2013-05-23 12:28:18
无花果。3B 在表面上显示被形成的 PEDOT 壳 PVC 毫微纤维的构词学，是统一的和由于 EDOT 的自然展览一种典型折子形状化学聚合。The thickness of the PEDOT shell on PVC-310, PVC-650 and PVC1100 were 56 7 nm, 45 5 nm and 22 4 nm, respectively, measured from TEM images of PEDOT tubes obtained by dissolving the PVC core with tetrahydrofuran.
|