求翻译：Figure 1a presents a cross-sectional scanning electron microscopy (SEM) image of the thus-prepared film. The absence of any PbI2 crystals protruding from the surface of the mesoporous anatase layer shows that our infiltration method leads to a structure in which the PbI2 is entirely contained within the nanopores of th是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Figure 1a presents a cross-sectional scanning electron microscopy (SEM) image of the thus-prepared film. The absence of any PbI2 crystals protruding from the surface of the mesoporous anatase layer shows that our infiltration method leads to a structure in which the PbI2 is entirely contained within the nanopores of th
问题补充： |
|
2013-05-23 12:21:38
图1a给出了这样制备的膜的横截面扫描电子显微镜（SEM ）图像。
|
|
2013-05-23 12:23:18
图1a提出因而准备的影片的一个横截扫描电子显微镜术(SEM)图象。推出从mesoporous anatase层数的表面的缺乏所有PbI2水晶表示，我们的滤渗方法导致PbI2在TiO2影片的nanopores内完全地包含的结构。
|
|
2013-05-23 12:24:58
图1a提出因而准备的影片的一个横截 (扫描) 电子显微镜术SEM图象。 推出从mesoporous anatase层数的表面的缺乏所有PbI2水晶表示，我们的滤渗方法导致PbI2在TiO2影片的nanopores内整个地包含的结构。
|
|
2013-05-23 12:26:38
图 1a 形象横断面扫描电子显微镜 (SEM) 因而准备影片。没有任何凸出的介孔锐钛型层从表面的 PbI2 晶体显示我们渗透方法导致 PbI2 完全包含在 TiO2 薄膜的纳米孔内结构。
|
|
2013-05-23 12:28:18
数字 1a 提出代表性仔细探索的电子显微镜方法 (SEM) 因此准备的电影的图像。从 mesoporous anatase 层的表面突出的任何 PbI2 水晶的缺席显示我们的渗透方法导致一种结构，其中 PbI2 在 TiO2 电影的毫微毛孔内完全被控制。
|