求翻译：The morphology of the fracture surface of the HAZ specimen after SCC testing is shown in Fig. 10, which was taken after tilting the specimen to show the SCC area more clearly. The stress corrosion crack did not go ahead straightly but deviated and seemed to go toward the fusion line. This kind of crack growth behavior 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The morphology of the fracture surface of the HAZ specimen after SCC testing is shown in Fig. 10, which was taken after tilting the specimen to show the SCC area more clearly. The stress corrosion crack did not go ahead straightly but deviated and seemed to go toward the fusion line. This kind of crack growth behavior
问题补充： |
|
2013-05-23 12:21:38
SCC试验后的HAZ试样的断裂表面的形态示于图。
|
|
2013-05-23 12:23:18
HAZ标本的破裂表面的形态学，在SCC测试在图10后显示，在掀动标本以后更加清楚显示SCC区域被采取。应力腐蚀裂缝没有继续平直地，但是偏离和似乎去往融合线。这种裂纹发展行为似乎是接近的键入在植物中观察的T-II崩裂，如图1.所显示。
|
|
2013-05-23 12:24:58
HAZ标本的破裂表面的形态学在SCC测试以后显示在。 10，在掀动标本以后更加清楚显示SCC地区被采取。 应力腐蚀裂缝没有继续平直地，但偏离和似乎去往融合线。 这种裂纹发展行为似乎是紧挨类型在植物中观察的T-II崩裂，如所显示。 1.
|
|
2013-05-23 12:26:38
SCC 测试显示在图 10 中，采取倾斜标本后，更清楚地显示的 SCC 区域后，HAZ 试样的断裂面形态。应力腐蚀裂纹没有继续下去直接但偏离，似乎往熔合线去。这种裂纹扩展行为似乎是接近 T-II 型裂缝观测在植物中，如图 1 所示。
|
|