求翻译：Well-behaved crack growth was observed in 2 ppm DO water both under trapezoidal loading or constant loading. There was an incubation time of about 220 h before the onset of the fast crack growth in 2 ppm DO water under the trapezoidal loading (SN01). After the SCC incubation period, crack growth rate increased with tim是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Well-behaved crack growth was observed in 2 ppm DO water both under trapezoidal loading or constant loading. There was an incubation time of about 220 h before the onset of the fast crack growth in 2 ppm DO water under the trapezoidal loading (SN01). After the SCC incubation period, crack growth rate increased with tim
问题补充： |
|
2013-05-23 12:21:38
在2ppm的观察乖巧的裂纹扩展双方在梯形荷载或恒载荷做防水。
|
|
2013-05-23 12:23:18
行为良好的裂纹发展在2 ppm被观察了浇灌两个在梯形装货或恒定的装货下。有孵出时候的大约220 h，在快速的裂纹发展的起始在2 ppm浇灌在梯形装货前(SN01)下。在SCC潜伏期以后，裂纹发展率增加与时间，并且能是几乎恒定的在长期相对地长期，例如，几数百几小时内或。
|
|
2013-05-23 12:24:58
行为端正的裂纹发展在2 ppm被观察了浇灌两个在梯形装货或恒定的装货之下。 在快速的裂纹发展的起始在2 ppm浇灌在梯形装货SN01之下之前，有孵出时候的大约220 (h)。 在SCC潜伏期以后，裂缝生长率增加了以时间，并且能是几乎恒定的在长期相对地长期，例如，几数百几小时之内或。 这样裂缝生长率被定义成平稳或quasi-steady状态裂缝生长率， CGRss。 它也被发现了，超过一个平稳的裂缝
|
|
2013-05-23 12:26:38
两个梯形荷载或恒定载荷下 2 ppm 做水中观察乖裂纹生长。2 ppm 的快速裂纹增长发病做水 （SN01） 在梯形荷载作用下过约 220 h 孵育时间。后 SCC 的潜伏期，裂纹扩展速率随时间增加而增加，可以在一段较长，例如，几百个小时或更长的时间内几乎不变。这种裂纹扩展速率的定义是稳定或准稳态状态裂纹扩展速率，CGRss。它也发现，多个裂纹稳态
|
|
2013-05-23 12:28:18
行为端正可卡因的成长在 2 ppm 中观察在装货，或是的 trapezoidal 下上水装货的常量。有大约 220 的一个酝酿时期 h 在 2 ppm 中的快可卡因的成长的开始在装货的 trapezoidal 下上水之前 ( SN01 )。SCC 酝酿时期使以时间被增强的增长率爆裂后和几乎在一段相对长时期内可能是持续的，例如，一些数百小时或更长。这样一个可卡因的增长率被定义为稳或者类似稳的州裂缝增长率， CGRss。也被找到那，超过一条稳的裂缝
|