求翻译：Undoped and In-doped ZnO thin films have been prepared on glass substrates from solutions of Zn(CH3CO2)22H2O in a mixture of deionized water and isopropyl alcohol by spray pyrolysis. Their optical, morphological and structural qualities have been studied and the effect of the preparation conditions discussed. It was sh是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Undoped and In-doped ZnO thin films have been prepared on glass substrates from solutions of Zn(CH3CO2)22H2O in a mixture of deionized water and isopropyl alcohol by spray pyrolysis. Their optical, morphological and structural qualities have been studied and the effect of the preparation conditions discussed. It was sh
问题补充： |
|
2013-05-23 12:21:38
在去离子水和异丙醇的利用喷雾热分解的混合物中不掺杂，并在掺杂的氧化锌薄膜已经制备在玻璃基板上，从由Zn （ CH 3 CO 2 ） 22H2O的解决方案。
|
|
2013-05-23 12:23:18
无掺杂和被掺杂的ZnO薄膜在从锌(CH3CO2)在被去离子的水和异丙醇混合物的22H2O的解答的玻璃基体准备了由浪花加热分解。他们的光学，形态和结构质量被学习了，并且准备条件的作用被谈论了。显示确定ZnO影片的参量主要因素是成长温度和铟含量。
|
|
2013-05-23 12:24:58
Undoped和在被掺杂的ZnO薄膜在玻璃基体在被去离子的水和(异丙醇)混合物准备了从锌CH3CO2 22H2O的解答由浪花加热分解。 他们的光学，形态和结构质量被学习了，并且准备条件的作用被谈论了。 它显示确定ZnO影片的参量主要因素是成长温度和铟含量。 成长温度625-675 K、铟掺杂水平的1-1.5 at.%的和0.1-0.2 mol前体集中1−1是更好达到ZnO影片以光学和结构质量如所需求为太阳能电池应用。
|
|
2013-05-23 12:26:38
在掺杂和非掺杂 ZnO 薄膜已经在玻璃衬底上从解决方案中的锌 (CH3CO2) 22H2O 在去离子的水和异丙醇的混合物中备喷雾热分解。其结构、 形态和光学素质进行了研究和讨论了制备工艺条件的影响。它是表明确定参数的 ZnO 薄膜的主要因素是生长温度和铟浓度。625 — — 675 K，铟掺杂水平的生长温度 1 — — 1.5 at.%和前体的浓度为 0.1 — — 0.2 mol 1 − 1 是最好实现 ZnO 薄膜的结构和光学素质作为太阳能电池应用程序需要。
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区