求翻译：pulsing) to 40.05% (100 Hz pulse frequency). As far as eutectic is concerned, the conventional TIG welding (without pulsing) produced eutectic of average size 12.8 μm (Fig. 2a) while pulse TIG welding at 25, 50 and 100 Hz produced eutectic of average size 15.6 μm,34.5 μm and 39.2 μm, respectively (Fig. 2b–d). An increa是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
pulsing) to 40.05% (100 Hz pulse frequency). As far as eutectic is concerned, the conventional TIG welding (without pulsing) produced eutectic of average size 12.8 μm (Fig. 2a) while pulse TIG welding at 25, 50 and 100 Hz produced eutectic of average size 15.6 μm,34.5 μm and 39.2 μm, respectively (Fig. 2b–d). An increa
问题补充： |
|
2013-05-23 12:21:38
脉冲）到40.05 ％ （100赫兹的脉冲频率）。
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
搏动) 到40.05% (100赫兹脉冲频率)。 就共晶有关，常规TIG焊接 (，不用搏动的) 被生产的共晶平均尺寸12.8 μm (。 2a) ，当脉冲TIG焊接在25， 50和100赫兹生产了共晶平均尺寸15.6 μm时， 34.5 μm和39.2 μm，分别 (。 2b-d). 在脉冲频率的增量增加了区域分数共晶。
|
|
2013-05-23 12:26:38
脉冲） 至 40.05%（100 赫兹脉冲频率）。共晶而言平均大小 12.8 μ m （图 2a） 同时常规 TIG 焊接 （无脉动） 产生的晶脉冲钨极氩弧焊在 25、 50 和 100 Hz 产生共晶的平均尺寸 15.6 μ m、 34.5 μ m 和 39.2 μ m，分别 （图 2b — — d）。共晶的脉冲频率增加的面积分数增加。
|
|
2013-05-23 12:28:18
pulsing) 到 40.05%(100 Hz 脉搏频率 )。就 eutectic 担心而言，焊接的传统的 TIG( 而没有 pulsing) 生产平均大小的 eutectic 12.8？m( 无花果。2a) 当脉搏焊接的对 25 的 TIG， 50 和 100 Hz 生产平均大小的 eutectic 15.6？m， 34.5？m 和 39.2？m，分别地 ( 无花果。2b-d ).在脉搏频率方面的增长增强面积的小部分 ofthe eutectic。
|