求翻译：Conventional TIG welding (without pulsing) produced aluminium grains with an average size of 50.5 μm (Fig. 2a) while pulse TIG welding at 25, 50 and 100 Hz produced aluminium grains of average size 40.2 μm, 17.8 μm and 10.2 μm, respectively (Fig. 2b–d). An increase in pulse frequency lowered area fraction of aluminium 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Conventional TIG welding (without pulsing) produced aluminium grains with an average size of 50.5 μm (Fig. 2a) while pulse TIG welding at 25, 50 and 100 Hz produced aluminium grains of average size 40.2 μm, 17.8 μm and 10.2 μm, respectively (Fig. 2b–d). An increase in pulse frequency lowered area fraction of aluminium
问题补充： |
|
2013-05-23 12:21:38
常规TIG焊接（无脉冲）在17.8微米和10.2微米，分别为25 ， 50和100产生的赫兹铝晶粒平均尺寸40.2微米的，生产的铝晶粒的50.5微米（图2a）的平均尺寸，而脉冲TIG焊接（
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
没有搏动的被生产的 (铝五谷的) 常规TIG焊接以50.5 μm的一平均尺寸 (。 2a) ，当脉冲TIG焊接在25， 50和100赫兹生产了平均尺寸40.2 μm时铝五谷， 17.8 μm和10.2 μm，分别 (。 2b-d). 在脉冲频率的增量降低了铝五谷的区域分数从71.2% (，无需搏动) 到40.05% (100赫兹脉冲频率)
|
|
2013-05-23 12:26:38
常规 TIG 焊接 （无脉动） 生产的铝晶粒平均大小为 50.5 μ m （图 2a） 同时脉冲钨极氩弧焊在 25、 50 和 100 Hz 生产铝晶粒的平均尺寸 40.2 μ m、 17.8 微米和 10.2 微米，分别 （图 2b — — d）。增加脉冲频率降低的面积分数铝颗粒从 71.2%（无脉动） 对 40.05%（100 赫兹脉冲频率）
|
|
2013-05-23 12:28:18
传统的 TIG 焊接 ( 而没有 pulsing) 以 50.5 的平均尺码生产铝颗粒？m( 无花果。2a) 当脉搏焊接的对 25 的 TIG， 50 和 100 Hz 生产平均大小的铝颗粒 40.2？m， 17.8？m 和 10.2？m，分别地 ( 无花果。2b-d ).在脉搏频率方面的增长从 71.2% 降低铝颗粒的面积的小部分 ( 而没有 pulsing) 到 40.05%(100 Hz 脉搏频率 )
|