求翻译：The Double H1150 (H1150 DBL) condition is used for NACE MR0175 constructions and for other applications where stress corrosion cracking is likely. The NACE specification MR0175 for sour environments requires the H1150M or the double H1150 treatments for wrought forms of 17-4 with a hardness of 33 HRC maximum. In late 1是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The Double H1150 (H1150 DBL) condition is used for NACE MR0175 constructions and for other applications where stress corrosion cracking is likely. The NACE specification MR0175 for sour environments requires the H1150M or the double H1150 treatments for wrought forms of 17-4 with a hardness of 33 HRC maximum. In late 1
问题补充： |
|
2013-05-23 12:21:38
双H1150 （ H1150 DBL ）条件用于NACE MR0175结构和其他应用中的应力腐蚀开裂的可能性较大。
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
双重H1150 (H1150 DBL) 情况使用为NACE MR0175建筑和为其他应用，应力腐蚀崩裂是可能的。 酸环境的NACE规格MR0175为17-4的加工的形式要求H1150M或双重H1150治疗以33 HRC最大值的坚硬。 在1993年末， CB7Cu-1铸件在H1150 DBL情况增加了到MR0175为保留组分，例如，笼子、插座、位子圆环和其他内部，阀门和管理者组分的非压力。 坚硬极限是30 HRC (310 HB) 最大值。
|
|
2013-05-23 12:26:38
双 H1150 (H1150 DBL） 条件用于 NACE MR0175 建筑和其他应用程序应力腐蚀开裂有可能的地方。酸性环境 NACE MR0175 规范要求 H1150M 或双 H1150 治疗锻制形式的 17 4 33 HRC 最大硬度。在 1993 年下半年，CB7Cu 1 铸件在 H1150 DBL 条件下被添加到 MR0175 对于非压力保留组件，如网箱、 插头、 阀座环和其他内部、 阀、 调节器组件。硬度极限是 30 HRC (310 HB） 最高。
|
|
2013-05-23 12:28:18
两倍的 H1150 ( H1150 DBL) 条件用于 NACE MR0175 解释和对使其爆裂的压力腐蚀状态可能的其他申请。NACE 规格用于发酵的环境的 MR0175 需要有 33 HRC 个最大值
|