求翻译：This will form reorientation polarization and energy dissipation due to enhanced ionic bonding character by Al doping. The more Al atoms contained in Ti3SiC2 contribute to the higher e0 and e00 , so 20% Al-doped sample has the greater values in e0 and e00 than 10% Al-doped sample是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
This will form reorientation polarization and energy dissipation due to enhanced ionic bonding character by Al doping. The more Al atoms contained in Ti3SiC2 contribute to the higher e0 and e00 , so 20% Al-doped sample has the greater values in e0 and e00 than 10% Al-doped sample
问题补充： |
|
2013-05-23 12:21:38
这将形成两极分化重新定位和能源消耗归因于铝掺杂增强离子键字符。
|
|
2013-05-23 12:23:18
这将形成再定位极化和消能由于改进的离子结合的性质通过Al掺杂。在Ti3SiC2包含的更多Al原子造成更高的e0和e00，因此20% Al被掺杂的样品比10% Al被掺杂的样品有很大的价值在e0和e00
|
|
2013-05-23 12:24:58
这将形成再定位极化和消能 由于改进的离子接合字符通过Al掺杂。 在Ti3SiC2包含的更多Al原子对更高的e0和e00贡献，因此20% Al被掺杂的样品比10% Al被掺杂的样品有更加了不起的价值在e0和e00
|
|
2013-05-23 12:26:38
这将形成增强离子键字符由 Al 掺杂调整偏振和能量耗散。更多的铝原子载 Ti3SiC2 和作出贡献高 e0 e00，因此 20%铝掺杂样品具有更大的价值 e0 和 e00 比 10%铝掺杂样品
|
|
2013-05-23 12:28:18
这将形成重新方位偏振和能量耗散由于由 Al 所作的被提高的离子结合文字的 用药物刺激。越是 Al 原子包含在 Ti3SiC2 中为更高的 e0 和 e00 撰稿，所以 20% 的 Al-doped 例子有更大 e0 和 e00 中的值 比 10% 的 Al-doped 例子
|