求翻译：20MnV6 either in the as supplied condition, or pre-hardened and tempered for higher core strength will respond successfully to nitriding due to the vanadium content. Typical case hardness achieved up to Rc 55.Nitriding is carried out at 490 oC - 530 oC followed by slow cooling (no quench) reducing the problem of distor是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
20MnV6 either in the as supplied condition, or pre-hardened and tempered for higher core strength will respond successfully to nitriding due to the vanadium content. Typical case hardness achieved up to Rc 55.Nitriding is carried out at 490 oC - 530 oC followed by slow cooling (no quench) reducing the problem of distor
问题补充： |
|
2013-05-23 12:21:38
20MnV6无论是在所提供的条件，或预硬化和回火更高芯强度将成功氮化响应由于钒含量。
|
|
2013-05-23 12:23:18
20MnV6在，因为由供应的情况或者前硬化和磨炼为更高的核心强度将顺利地反应氮化由于钒内容。
|
|
2013-05-23 12:24:58
20MnV6在，因为由供应的情况或者为更高的核心强度前硬化和磨炼将成功地反应氮化由于钒内容。 典型的案件坚硬达到由Rc 55.Nitriding决定被执行在490 oC - 530 oC由缓慢冷却跟随 (没有熄灭) 减少畸变的问题。因此零件可能用机器制造到近的最后的大小，留下仅研的容忍。如果前硬化和总使用被磨炼的原料保证被使用的回火温度是至少15oC在氮化温度之上。
|
|
2013-05-23 12:26:38
正在翻译，请等待...
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区