求翻译：This paper analyzes the characteristics and difficulties of complex steel composite structure cast in C70 concrete,in accordance with the technical line of high-performance large-volume fly ash concrete were concrete mix design, and comparison test of expansive agent and shrinkage-reducing agent and curing agent in th是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
This paper analyzes the characteristics and difficulties of complex steel composite structure cast in C70 concrete,in accordance with the technical line of high-performance large-volume fly ash concrete were concrete mix design, and comparison test of expansive agent and shrinkage-reducing agent and curing agent in th
问题补充： |
|
2013-05-23 12:21:38
本文分析的特点和复杂的钢复合结构，铸于C70混凝土的困难，按照高性能大掺量粉煤灰混凝土的技术路线是混凝土配合比设计和膨胀剂和减缩剂的对比测试和
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
本文分析特征，并且在C70混凝土熔铸的复杂钢综合结构困难，与高性能大容量的飞烟混凝土符合技术线是混凝土混合料设计和膨胀的代理比较审检法和收缩减少代理和固化剂在功能在变化的温度效应之下。 结果表示，在增加一定数量以后前吸收剂水内在保护代理， C70内在铸件自已变紧密大容量混凝土自生的收缩可能符合工程学质量管理要求。
|
|
2013-05-23 12:26:38
本文分析特性和困难复杂钢复合结构 C70 混凝土，大体积粉煤灰高性能混凝土的技术路线现浇混凝土配合比设计和膨胀剂和减缩剂和固化剂的功能在不同的温度效应下的对比试验。结果表明添加一定量的预吸水内部保护剂后, C70 内铸造自密实混凝土的自收缩大体积可以满足工程的质量控制要求。
|
|
2013-05-23 12:28:18
这篇文章按照高性能的技术线在 C70 混凝土中分析复杂钢铁复合结构投的特征和困难大量飞行灰混凝土是具体的掺和设计，广阔的代理和 shrinkage 减少的代理的比较测试和在改变温度的效果下在功能中治好代理。结果在加某种程度的能吸收前的水之后显示那内部保存代理， C70 内部投掷自我压缩大量混凝土的 autogenous shrinkage 中可能符合设计质量管理要求。
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区