求翻译：This paper analyzes the characteristics and difficulties of C70 cast in concretecomplex steel composite structure,in accordance with the technical line of high-performance large-volume fly ash concrete were concrete mix design, and comparison test of expansive agent and shrinkage-reducing agent and curing agent in th是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
This paper analyzes the characteristics and difficulties of C70 cast in concretecomplex steel composite structure,in accordance with the technical line of high-performance large-volume fly ash concrete were concrete mix design, and comparison test of expansive agent and shrinkage-reducing agent and curing agent in th
问题补充： |
|
2013-05-23 12:21:38
本文分析的特点和C70铸于concretecomplex钢复合结构的困难，按照高性能大掺量粉煤灰混凝土的技术路线是混凝土配合比设计和膨胀剂和减缩剂和固化对比测试
|
|
2013-05-23 12:23:18
本文分析特征，并且C70困难在concretecomplex钢综合结构熔铸了，符合高性能大容量的飞烟混凝土技术线是混凝土混合料设计和膨胀的代理比较审检法和收缩减少代理和固化剂在功能在变化的温度效应下。
|
|
2013-05-23 12:24:58
本文分析特征，并且在concretecomplex钢综合结构熔铸的C70困难，与高性能大容量的飞烟混凝土符合技术线是混凝土混合料设计和膨胀的代理比较审检法和收缩减少代理和固化剂在功能在变化的温度效应之下。 结果表示，在增加一定数量以后前吸收剂水内在保护代理， C70内在铸件大容量自已变紧密的混凝土自生的收缩可能符合工程学质量管理要求。
|
|
2013-05-23 12:26:38
本文分析了特点和困难 C70 concretecomplex 钢复合结构问题，根据高性能大体积粉煤灰混凝土的技术路线现浇混凝土配合比设计和膨胀剂和减缩剂和固化剂的功能在不同的温度效应下的对比试验。结果表明添加一定量的预吸水内部保护剂后, C70 内浇大体积的自密实混凝土的自收缩可以满足工程的质量控制要求。
|
|
2013-05-23 12:28:18
这篇文章按照高性能的技术线在 concretecomplex 钢合成物结构分析 C70 投的特征和困难大量飞行灰混凝土是具体的掺和设计，广阔的代理和 shrinkage 减少的代理的比较测试和在改变温度的效果下在功能中治好代理。结果在加某种程度的能吸收前的水之后显示那内部保存代理， C70 内部投掷大量自我压缩混凝土的 autogenous shrinkage 中可能符合设计质量管理要求。
|