求翻译：Basing on the UCS results of samples after curing 3, 7, 14, 28, and 90 days, the effect of curing time on UCS of cement-soil was studied. As Fig.2 shows, the compression strength of soil-cement increases with curing time. For cement treated soil, as the hydrolysis and hydration reaction (Eqs.(1)-(7)) proceed with curin是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Basing on the UCS results of samples after curing 3, 7, 14, 28, and 90 days, the effect of curing time on UCS of cement-soil was studied. As Fig.2 shows, the compression strength of soil-cement increases with curing time. For cement treated soil, as the hydrolysis and hydration reaction (Eqs.(1)-(7)) proceed with curin
问题补充： |
|
2013-05-23 12:21:38
固化3，7， 14 ，28，和90天后基础上样品的UCS结果，固化时间对水泥土UCS的影响进行了研究。
|
|
2013-05-23 12:23:18
根据样品的UCS结果在治疗3以后， 7， 14， 28和90天，治愈时间的作用对水泥土壤UCS被学习了。当Fig.2显示，土壤水泥压缩力量增加与治愈时间。对水泥土壤，把加水分解和水合作用反应(Eqs看作。(1) - (7))继续进行治愈时间、更多C-S-H、C-A-H和6CaO•Al2O 3•Fe2O 3•在soilcement形成的12H2O。所以， soilcement压缩力量增加与治愈时间。
|
|
2013-05-23 12:24:58
根据样品的UCS结果在治疗3以后， 7， 14， 28和90天，治愈时间的作用在水泥土壤UCS被学习了。 和展示，土壤水泥增量压缩力量以治愈时间。 为水泥土壤，把加水分解和水合作用反应 (Eqs。(1看作)-( 7)) 继续进行治愈时间、更多C-S-H、C-A-H和6CaO•氧化铝•Fe2O 3•12H2O在soilcement形成了。 所以， soilcement压缩力量增加以治愈时间。 另外， SO4在土壤 (如表2所显示) 可能导致C-A-H和C-S-H，将生产过剩Ca6Al 2(那么4) 3( OH) 12•26H 2O，当组合与3CaO•Al3O3作为Eq。 (9)
|
|
2013-05-23 12:26:38
基于样本的 UCS 结果后固化 3、 7、 14、 28、 90 天，固化时间对水泥土抗压强度的影响进行了研究。如图 2 所示，水泥土的压缩强度随固化时间。水泥土，视为水解和水化反应 （情商的人。 （1)-(7)) 进行固化时间、 更多 C-S-H、 C-A-H 和 6CaO•Al2O 3•Fe2O 3•12H2O 在拌中形成。因此，拌的压缩强度随固化时间。此外，SO4 （如表 2 所示） 的土壤中可以导致 C-A-H 和 C-S-H，会过度生产 Ca6Al 2 （所以 4) 3(OH) 12•26H 2O 时结合 3CaO•Al3O3 作为情商 (9)。
|
|