求翻译：Analyzing Figure 2 taking into account the visual-analytical chronometry of the cooling time of the weld pool, it was established that welding in these conditions results in all likelihood in the formation of defects with a size of d , 0.25 mm in the welded joints. This is confirmed by the results of X-ray diffraction 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Analyzing Figure 2 taking into account the visual-analytical chronometry of the cooling time of the weld pool, it was established that welding in these conditions results in all likelihood in the formation of defects with a size of d , 0.25 mm in the welded joints. This is confirmed by the results of X-ray diffraction
问题补充： |
|
2013-05-23 12:21:38
判断图2考虑到熔池的冷却时间的视觉分析比色法，它建立在这些条件导致在形成缺陷具有大小为d的0.25毫米的焊接接头的所有可能性的焊接。
|
|
2013-05-23 12:23:18
分析考虑到焊接水池的冷却时间的视觉分析测时学的图2，在这些情况结果建立了很有可能焊接在瑕疵的形成与d，在焊接处的0.25 mm的大小的。这由被焊接的标本的X光衍射检查的结果证实。
|
|
2013-05-23 12:24:58
分析考虑到焊接水池的冷却时间的视觉分析测时学的图2，它在这些情况结果在焊接处建立了很有可能焊接在瑕疵的形成以d， 0.25毫米的大小。 This is confirmed by the results of X-ray diffraction inspection of the welded specimens.
|
|
2013-05-23 12:26:38
图 2 考虑到视觉分析的测时的焊接熔池的冷却时间的分析，建立了在这些条件下焊接结果在所有的可能性，在一个大小为 d，0.25 毫米的焊接接头缺陷的形成。通过对焊接试样的 x 射线衍射商检的结果证实了这一点。
|
|
2013-05-23 12:28:18
分析图 2 考虑冷却的时间的视觉分析的测时法焊接池，它被建立在这些条件方面的那焊接以一大小的 d，在焊接关节中的 0.25 毫米在缺陷的编队中导致所有可能性。这被焊接样本的 X 射线衍
|