求翻译：It is interesting to compare the SHR level observed here with those in TWIP steels, where intense mechanical twinning is a typical feature. In TWIP steels, SHR decreases first rapidly with strain but remains at a high level of 2200–2300 MPa, see e.g. [52].Hamada et al. [53] observed SHR around 3000 MPa and de las Cueva是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
It is interesting to compare the SHR level observed here with those in TWIP steels, where intense mechanical twinning is a typical feature. In TWIP steels, SHR decreases first rapidly with strain but remains at a high level of 2200–2300 MPa, see e.g. [52].Hamada et al. [53] observed SHR around 3000 MPa and de las Cueva
问题补充： |
|
2013-05-23 12:21:38
有趣的是，在这里观察到的那些TWIP钢中，其中强烈的机械孪晶是一个典型的特征与SHR水平进行比较。
|
|
2013-05-23 12:23:18
被观察的SHR水平这里与那些比较在TWIP钢是有趣的，强烈机械孪生是一个典型的特点。在TWIP钢，迅速首先SHR减退与张力，但是依然是在高级2200-2300 MPa，看见[即52]。滨田[53]等注意到在3000 MPa和de las奎瓦斯附近的SHR [54]等报告了2650-2730 MPa的SHR水平。因此，获得的SHR这里低于普通的highMn TWIP钢的出席者。滨田等。
|
|
2013-05-23 12:24:58
这里被观察的SHR水平与那些比较在TWIP钢是有趣的，强烈机械孪生是一个典型的特点。 在TWIP钢，迅速首先SHR减退以张力，但依然是在高级2200-2300 MPa，看见即。 (52). Hamada等。 (53) 在3000 MPa和de las Cuevas附近等观察了SHR。 (54个) 报告的SHR水平的2650-2730 MPa。 因此，这里获得的SHR低于出席者在普通的highMn TWIP钢。 Hamada等。 (45) 表示，变形孪生如此提高低Ni哥斯达黎加Mn类型201和201L奥氏体的不锈钢的SHR和伸长。 对应于a0马氏体的微弱的形成的典型的SHR水平与变形孪生一起是
|
|
2013-05-23 12:26:38
它很有趣比较 SHR 水平观察这里那些 TWIP 钢中激烈的机械孪晶在哪里的典型特征。TWIP 钢中 SHR 跌幅首先迅速与应变但仍维持在高水平的 2200年-2300年精神创伤和痛苦，例如见 [52]。滨田 et al.[53] 观察自发性高血压大鼠周围 3000 MPa 和 de las 奎瓦斯 et al.[54] 报道 2650年-2730 MPa SHR 水平。因此，这里获得 SHR 是低于普通 highMn TWIP 钢中的那些礼物。滨田 et al.[45] 表明，形变孪晶提高了自发性高血压大鼠与伸长率的低镍铬 — — 锰 201 和 201 L 型奥氏体不锈钢。典型的自发性高血
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区