求翻译：It should be noted that when the deformation is carried out at 1050 ℃ and 0.001 s–1, the deformed specimen shows not only the recrystallized grains, but also amount of secondary phases, as indicated in Fig. 5(c). SEM micrograph shows that the plate-like and unevenly distributed precipitates of 1-8 μm in size existed in是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
It should be noted that when the deformation is carried out at 1050 ℃ and 0.001 s–1, the deformed specimen shows not only the recrystallized grains, but also amount of secondary phases, as indicated in Fig. 5(c). SEM micrograph shows that the plate-like and unevenly distributed precipitates of 1-8 μm in size existed in
问题补充： |
|
2013-05-23 12:21:38
应当注意的是，如果由变形是在1050℃和0.001 S-1，变形的试样不仅显示了再结晶的晶粒，而且第二相的量，如图8中所示。
|
|
2013-05-23 12:23:18
值得注意的是，，当变形被执行在1050 ℃和0.001 s-1时，被扭屈的标本如图5 (c)所示显示不仅被重结晶的五谷，而且相当数量次要阶段。SEM微写器表示， 1-8 μm板状和参差不齐地分布的沉淀物在大小上存在了于晶界和内部，如图6 (a)所显示。根据EDS发生(图。
|
|
2013-05-23 12:24:58
值得注意的是，，当变形被执行在1050年℃和0.001 s-1时，被扭屈的标本显示不仅被重结晶的五谷，而且相当数量次要阶段，如被表明在。 5( c)。 SEM微写器表示， 1-8 μm plate-like和参差不齐地分布的沉淀物在大小存在了于晶界和内部，如所显示。 6( a)。 根据EDS收效 (。 6( b)) 和报告了19的早先(调查)，沉淀物在哥斯达黎加和Mo认为是斯格码阶段富有。 虽然沉淀物可能制约晶粒生长，流程重音可能增加的归结于硬化在热的变形期间的降雨雪的作用。 预期，流程重音曲线获得在1050年℃和0.001 s-1 (。 2( b)) 显示在重音的增量，当真实的张力超出0.8
|
|
2013-05-23 12:26:38
应指出的是变形进行时在 1050年 ℃、 0.001 s — — 1，变形的试样表明不仅再结晶的晶粒，而且第二相的数量作为表示在图披露。扫描电镜显微图像显示 1 8 微米大小的板状和均匀沉淀存在在晶界和室内，图 6 (a) 所示。EDS 成果的基础上 （图 6(b)) 和以前的调查已报道 [19]，析出物被认为是富含 Cr 和密苏里州的西格玛阶段虽然析出物能有效抑制晶粒生长，流动应力能增加热变形过程中的沉淀硬化效应。不出所料，流动应力曲线在 1050年 ℃、 0.001 s — — 1 （图 2(b))） 显示，增加压力时真应变超过 0.8，和热变形应避免这种情况下。需要进一步的研究来说明 6
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区