求翻译：The specimens deformed under the conditions in the second and third domains show the complete dynamic recrystallization accompanied with the grain growth, as shown in Figs. 5(d) and (e). The wavy or irregular grain boundaries can be easily observed. These two domains occur at temperatures which are close to the dissolu是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The specimens deformed under the conditions in the second and third domains show the complete dynamic recrystallization accompanied with the grain growth, as shown in Figs. 5(d) and (e). The wavy or irregular grain boundaries can be easily observed. These two domains occur at temperatures which are close to the dissolu
问题补充： |
|
2013-05-23 12:21:38
在第二个和第三个结构域的条件下而变形的试样示出了完整的动态再结晶伴随有晶粒生长，如图。
|
|
2013-05-23 12:23:18
在第二个和第三个领域的条件下被扭屈的标本显示完全动态再结晶伴随于晶粒生长，如Figs. 5所显示(d)和(e)。波浪或不规则的晶界可以容易地被观察。这两个领域发生在是接近溶解温度沉淀物的温度。
|
|
2013-05-23 12:24:58
在条件下被扭屈的标本在第二个和第三个领域显示完全动态再结晶伴随于晶粒生长，如Figs.所显示。 5( d) 和 (e)。 波浪或不规则的晶界可以容易地被观察。 这二个领域发生在是紧挨溶解温度沉淀物的温度。 次要阶段开始进入溶解在热的变形期间，并且晶粒生长可观地被促进以温度在1100年℃之上和变形率在0.1 s-1以下。 它能被看见被重结晶的五谷的部分重大成长导致了为合金物产是不赞同的混杂的颗粒结构。
|
|
2013-05-23 12:26:38
在第二和第三个域条件下变形的标本显示完整的动态再结晶晶粒的生长，伴随图 5 (d) 和 (e) 所示。波浪状或不规则的晶界可以很容易观察到。这两个域时，温度与析出相的溶解温度接近的。中学阶段开始进入在热变形过程中的溶出度和晶粒生长大大促进在温度超过 1100年 ℃ 和应变速率低于 0.1 s – 1。可以看出部分再结晶颗粒的显著增长有诱导的混的晶结构不利于合金的性能。
|
|