求翻译：TEM microphotographs of the synthesized MPCPs are shown in Figure 5(I). The amount of SDS had a notable effect on the Fe3O4 encapsulation degree, particle size, and PSD of the MPCPs [Fig. 5(II)]. With 2% SDS, the Fe3O4 encapsulation degree was very high, and some BMPs and few PPPs were observed. At 3% SDS, the encapsul是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
TEM microphotographs of the synthesized MPCPs are shown in Figure 5(I). The amount of SDS had a notable effect on the Fe3O4 encapsulation degree, particle size, and PSD of the MPCPs [Fig. 5(II)]. With 2% SDS, the Fe3O4 encapsulation degree was very high, and some BMPs and few PPPs were observed. At 3% SDS, the encapsul
问题补充： |
|
2013-05-23 12:21:38
正在翻译，请等待...
|
|
2013-05-23 12:23:18
被综合的MPCPs的TEM显微照片在表5 (I)显示。相当数量SDS有对MPCPs [图5的Fe3O4封闭程度、颗粒大小和PSD的著名的作用(II)]。2% SDS， Fe3O4封闭程度非常高，并且有些BMPs和少量PPPs被观察了。在3% SDS， Fe3O4的封闭是成功的，并且BMPs和PPPs未被观察。
|
|
2013-05-23 12:24:58
被综合的MPCPs的TEM显微相片在表5 I(显示)。 相当数量SDS有一个著名的作用在MPCPs的磁铁矿封闭程度、微粒大小和PSD (。 5( II))。 与2% SDS，磁铁矿封闭程度是非常高，并且某一BMPs和少量PPPs被观察了。 在3% SDS，磁铁矿的封闭是成功的，并且BMPs和PPPs未被观察。 当SDS的集中是4%，磁铁矿封闭程度低于那与2和3%，因为BMPs的数字增加了。 与5% SDS，磁铁矿封闭程度低于那与2和3%，并且很大数量的BMPs被观察了。
|
|
2013-05-23 12:26:38
所示的合成 MPCPs 透射电镜显微图理解该词。SDS 量有显著影响 Fe3O4 封装程度、 粒径和 PSD 的 MPCPs [图 5(II)]。2%的 SDS，Fe3O4 封装程度是很高，和观察一些骨形态发生蛋白和几个公私伙伴关系。在 3%的 SDS，四氧化三铁的封装是成功的并观察 BMPs 既公私伙伴关系。4%的 SDS 浓度时，Fe3O4 封装程度较低比 2 与 3 ％ 是因为骨形态发生蛋白的数量增加。5%的 SDS，与大量的骨形态发生蛋白观察和 Fe3O4 封装程度是远远低于 2 和 3%。
|
|