求翻译：The reason for the lattice constant of the cerium oxide type of crystal to be limited to the range of 0.544 to 0.560 nm is that, according to the inventors\' investigation, with the lattice constant less than 0.544 nm the polished value is increased, but scratches occur in the polished surface, whereas with the lattice是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The reason for the lattice constant of the cerium oxide type of crystal to be limited to the range of 0.544 to 0.560 nm is that, according to the inventors\' investigation, with the lattice constant less than 0.544 nm the polished value is increased, but scratches occur in the polished surface, whereas with the lattice
问题补充： |
|
2013-05-23 12:21:38
究其原因，晶体的氧化铈型的晶格常数要限制在0.544至0.560纳米的是，根据本发明人\'调查，用晶格常数小于0.544纳米抛光值增加，但
|
|
2013-05-23 12:23:18
水晶的铈氧化物类型的格子常数的原因被限制到0.544到0.560毫微米的范围是那，根据发明者\\ ‘调查，与格子常数少于0.544毫微米优美的价值增加，但是抓痕在优美的表面发生，而与格子常数超过0.560毫微米抓痕不发生，但是充足的优美的价值不可能得到
|
|
2013-05-23 12:24:58
水晶的铈氧化物类型的格子常数的原因被限制到0.544到0.560毫微米的范围是那，根据发明者\ ‘调查，以格子常数少于0.544毫微米polished价值增加，但抓痕在polished表面发生，而以格子常数超过0.560毫微米抓痕不发生，但是充足的polished价值不可能得到
|
|
2013-05-23 12:26:38
原因为晶格常数的铈氧化型的晶体的 0.544 到 0.560 范围仅限于 nm 是，根据 inventors\' 调查与晶格常数小于 0.544 纳米抛光的值的上升，但划痕发生在抛光的表面，而与晶格常数比 0.560 nm 无划痕发生但不能获得足够的抛光的价值
|
|
2013-05-23 12:28:18
限于 0.544 到 0.560 岁之间的水晶的铈氧化物类型的格子架常量的理由 nm 是那，根据 inventors\ ' 调查，以格子架常量少于 0.544 nm 被擦亮的价值被增强，但是抓在被擦亮的表面发生，而以格子架常量超过 0.560 nm 没有抓痕出现，但是足够被擦亮的价值不能被获取
|