求翻译：The oxidation performance of the coatings was evaluated by isothermal oxidation at 1700 °C in air using a DF-2005-7 high temperature test platform. The specimens (70 × 8 × 1 mm) were heated to oxidation temperature using a large electric current. The oxidation time reported in this study represents the cumulative durat是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The oxidation performance of the coatings was evaluated by isothermal oxidation at 1700 °C in air using a DF-2005-7 high temperature test platform. The specimens (70 × 8 × 1 mm) were heated to oxidation temperature using a large electric current. The oxidation time reported in this study represents the cumulative durat
问题补充： |
|
2013-05-23 12:21:38
涂层的氧化性能通过恒温氧化在1700℃下在空气中使用的DF- 2005-7高温测试平台进行评价。
|
|
2013-05-23 12:23:18
使用DF-2005-7高温测试平台，涂层的氧化作用表现由在1700 °C的等温氧化作用评估在空气。标本(70 × 8 × 1 mm)使用大电流，被加热了对氧化作用温度。在这项研究中报告的氧化作用时间代表渐增暴露时间在1700 °C，直到涂层是分隔的，认为标本的铌合金基体变得氧化。
|
|
2013-05-23 12:24:58
涂层的氧化作用表现由等温氧化作用在空气评估在1700年°C使用DF-2005-7高温度测试平台。 标本 (70 × 8 × 1毫米) 被加热了到氧化作用温度使用大电流。 氧化作用时间在这项研究中报告了代表渐增暴露时间在1700年°C，直到涂层是分隔的，认为标本的铌合金基体变得氧化。
|
|
2013-05-23 12:26:38
使用 DF-2005年-7 高温测试平台的空气中，1700 ℃ 等温氧化法评价涂层的氧化性能。标本 （70 × 8 × 1 毫米） 又被加热到氧化温度使用大的电流。在这项研究报告的氧化时间表示累积暴露在 1700 ° C 的直到涂层分离，被认为是当成为氧化铌合金基体的标本。
|
|
2013-05-23 12:28:18
层的氧化表现在使用一个 DF-2005-7 高温度测试平台的空中在 1700 ° C 处被等温的氧化评价。样本 (70 x 8 x 1 毫米 ) 被加热到使用一股大电流的氧化温度。氧化时间在这项研究中报告直到层在 1700 ° C 代表暴露的累积持续被分离，考虑当铌合金样本的 substrate 成为氧化。
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区