求翻译：A carbon enrichment of the samples can also be seen in the air case (see Figure 5), which is typical for superheater materials after a certain time in power plants, however the dimension of the phenomena varies significantly in case of the oxy-fuel samples which allows to think it is not only caused by the diffusion of是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
A carbon enrichment of the samples can also be seen in the air case (see Figure 5), which is typical for superheater materials after a certain time in power plants, however the dimension of the phenomena varies significantly in case of the oxy-fuel samples which allows to think it is not only caused by the diffusion of
问题补充： |
|
2013-05-23 12:21:38
样品的碳富集，也可在空气中的情况下看到的（见图5） ，这是典型的过热器的材料在一定时间后在发电厂，但是这种现象的尺寸的情况下的氧 - 燃料样品的显著变化
|
|
2013-05-23 12:23:18
样品的碳充实在空气盒能也看(参见图5)，为过热装置材料是典型的在有些时光以后在能源厂，然而准许认为现象的维度在oxy燃料样品的情况下极大变化它由被夺取的碳的扩散不仅造成在往它的表面，但是更高的二氧化碳部份压力的作用的合金矩阵在oxy燃料事例。
|
|
2013-05-23 12:24:58
样品的碳充实在空气盒能也看 (看图5)，为过热装置材料是典型的在有些时光以后在能源厂中，然而准许认为现象的维度在oxy燃料样品的情况下极大变化它由被夺取的碳的扩散不仅造成在合金矩阵往它的表面，但更高的二氧化碳部份压力的作用在oxy燃料事例。
|
|
2013-05-23 12:26:38
碳富集的样品，也可以见于空气的情况下 （见图 5），这就是典型的后一段时间的力量植物，然而现象的维度差异显著对于氧燃料样品，可认为它不只捕获在对其表面合金基体中的碳的扩散所造成，但疗效更高 CO2-局部压力在含氧燃料情况下的过热器材料。
|
|
2013-05-23 12:28:18
例子的碳富裕可以也在空中被看见案例 ( 看到图 5)，为超加热器材料是典型的在发电厂中的某个时间之后，然而，现象的尺寸明显变化以防 oxy 燃料的例子那允许认为它不仅仅由朝其表面在合金矩阵方面被获取的碳的散布造成但是在 oxy 燃料的案例中的更高 CO2 泛音的压力的一种效果。
|