求翻译：Following the work of Ref. [12], the microstructure variation behavior of superalloy IN718 was studied in the present work on the basis of isothermal constant- speed compression tests conducted using a computer- controlled MTS machine at temperatures of from 960–1040°C, with initial strain rates of from 0.001–1.0 s−1, 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Following the work of Ref. [12], the microstructure variation behavior of superalloy IN718 was studied in the present work on the basis of isothermal constant- speed compression tests conducted using a computer- controlled MTS machine at temperatures of from 960–1040°C, with initial strain rates of from 0.001–1.0 s−1,
问题补充： |
|
2013-05-23 12:21:38
下列参考文献的工作。
|
|
2013-05-23 12:23:18
在参考后工作。
|
|
2013-05-23 12:24:58
从事参考工作。 (12)， superalloy IN718微结构变异行为在当前工作被学习了根据使用一个计算机控制的MTS机器进行的等温匀速压缩试验在温度从960-1040°C，以从0.001-1.0 s−1的初应变率，到工程学对 (高度的张力减少) 从0.1-0.7。 在粒度分析了热变形参量的作用，并且模型是devel- oped描述双重微结构和表达粒度和热变形参量之间的关系。
|
|
2013-05-23 12:26:38
继文献 [12] 的工作，显微组织变化规律的镍基高温合金 IN718 等温恒速压缩试验的基础上目前的工作进行了研究使用 MTS 机微机控制，温度从 960 — — 1040 ° C，初始应变率从 0.001-1.0 进行 s−1，对工程菌株 （减少高度） 的从 0.1-0.7。热变形参数对晶粒尺寸的影响进行了分析和模型是管式描述的双面打印器的微观结构和表达的晶粒尺寸与热变形参数之间的关系。
|
|
2013-05-23 12:28:18
随着 Ref 的工作。(12)，超合金 IN718 的微型结构变化行为在等温持续速度压缩的基础上在目前的工作中被研究检查召开使用一台电脑以温度控制 MTS 机器从 960-1040 ° C，以最初类型比率到设计类型，从 0.001-1.0 s-1 ( 高度的缩减 ) 从 0.1-0.7。热变形的参数的效果在谷的大小上被分析和一个模型是 devel 的 oped 描述双工微型结构，表达谷的大小和热变形的参数之间的关系。
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区