求翻译:In general, increasing particle size will reduce the contact surface between powders and restrain the formation of ZrC and ZrB2,though the value of G◦for Eq. (1) is negative. As B4C reaches 14um, the maximum peak temperature corresponding to theZr–B4C reaction is above 1182◦C because high temperature favorsthe reacti是什么意思?

待解决 悬赏分:1 - 离问题结束还有
In general, increasing particle size will reduce the contact surface between powders and restrain the formation of ZrC and ZrB2,though the value of G◦for Eq. (1) is negative. As B4C reaches 14um, the maximum peak temperature corresponding to theZr–B4C reaction is above 1182◦C because high temperature favorsthe reacti
问题补充:

  • 匿名
2013-05-23 12:21:38
通常,增加粒度会降低粉末之间的接触面,抑制的ZrC和ZrB2的形成,虽然?G◦for公式的值。
  • 匿名
2013-05-23 12:23:18
正在翻译,请等待...
  • 匿名
2013-05-23 12:24:58
正在翻译,请等待...
  • 匿名
2013-05-23 12:26:38
一般情况下,粒子大小的增加将减少接触表面间粉末,并抑制形成 ZrC 和 ZrB2,虽然 G◦for 方程 (1) 值为负。B4C 到达 14u m,对应于 theZr — — B4C 反应的最大峰值温度大于 1182◦C 因为高温度总是宠爱那些反应性的粉末,往往是不完整的低于 1250◦C(Fig.4b)。其结果是,更多锆留在 DSC 的产品,和由此产生的 ZrC 和 ZrB2 下降 (图 5b)。进一步增加大小的 B4C 到 28 米锆与 B4C 呆滞的固态反应的结果。这产生了小小的 ZrC 和 ZrB2 (图 5 c)。小数量的热发布经 ZrC ZrB2dissipatedinto 周围的