求翻译：After heating the 14um B4C samples to 973◦C, a slight exothermic peak emerges (Fig. 6a). Based on the Cu–Zr binary phase diagram [21], the crystal melting transformation Cu8Zr3→Cu51Zr14+ liquid occurs at 975◦C, which is endothermic. The liq-uid will provide an easier route for the movement of particles.Then, B4C grain是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
After heating the 14um B4C samples to 973◦C, a slight exothermic peak emerges (Fig. 6a). Based on the Cu–Zr binary phase diagram [21], the crystal melting transformation Cu8Zr3→Cu51Zr14+ liquid occurs at 975◦C, which is endothermic. The liq-uid will provide an easier route for the movement of particles.Then, B4C grain
问题补充： |
|
2013-05-23 12:21:38
加热14U ？米B4C样品973◦C后，轻微放热峰出现（图6a） 。
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
正在翻译，请等待...
|
|
2013-05-23 12:26:38
加热 14u m B4C 样品到 973◦C 后, 一种轻微的放热峰出现 (图 6a)。基于铜 — — 锆二元相图 [21]，晶体熔化转化 Cu8Zr3→Cu51Zr14 + 液发生在 975◦C，这是吸热。免除 uid 将提供更容易的途径，为粒子的运动。然后，B4C 颗粒溶解和扩散到铜 — — 锆熔体含锆形成更稳定的 ZrC 和 ZrB2while releasingheat andreacted。这些综合的反应导致弱 exothermicpeak 在 973◦C (图 6a)。因此，Cu51Zr14、 ZrC 和 ZrB2increases 在 973◦C 淬火的产品中的内容 （图 7a）
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区