求翻译：Since high Ts results in the increase of (101)oriented FePt grains, the in-plane ½110 direction of the MgO (110) substrate becomes the easy magnetization direction compared with the in-plane [001] direction. As shown in Fig. 3(c), the difference between the magnetization curves measured along the MgO [001] and MgO ½110是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Since high Ts results in the increase of (101)oriented FePt grains, the in-plane ½110 direction of the MgO (110) substrate becomes the easy magnetization direction compared with the in-plane [001] direction. As shown in Fig. 3(c), the difference between the magnetization curves measured along the MgO [001] and MgO ½110
问题补充： |
|
2013-05-23 12:21:38
由于高的TS产生的（101）取向的FePt晶粒的增加， MgO的面内½110方向（110）基片变得易磁化方向的平面内[001]方向进行比较。
|
|
2013-05-23 12:23:18
因为高实验装置导致(101)针对的FePt五谷增量， MgO (110个)基体的飞机½ 110方向成为容易的磁化方向比较飞机[001个]方向。如图3所显示(c)，沿MgO [001]和MgO ½被测量的磁化曲线之间的区别110方向为实验装置¼ 500 C.减少。
|
|
2013-05-23 12:24:58
因为高茶匙导致101针对的FePt (五谷)增量， MgO 110基体的在飞机½ 110 (方向) 成为容易的磁化方向比较在飞机 (001) 方向。 如所显示。 3( c)，沿MgO 001和MgO ½被测量的 (磁化) 曲线之间的区别110方向为茶匙¼ 500 C.减少。 这建议茶匙¼ 500 C不是适当的作为坚硬磁性层数在交换春天影片，因为在飞机单轴的磁性各向异性现象是根本固定毗邻Py层数的磁化沿一个方向。
|
|
2013-05-23 12:26:38
因为高 Ts 导致的 （101） 增加面向 FePt 谷物，MgO （110） 基片的飞机在 ½110 方向成为相比在飞机 [001] 方向的易磁化方向。图 3 (c) 所示，沿着 MgO [001] 和 MgO ½110 方向测量磁化曲线之间的差异减少为 Ts ¼500 C.这表明 Ts ¼500 C 不适合作为交换春天电影中有一层坚硬的磁性，因为面内单轴磁各向异性，修复沿一个方向相邻的 Py 层的磁化至关重要。
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区