求翻译：In this approach, we successfully use nucleophilic addition and 2-step hydrolysis for nano-meter sized zinc orthosilicate. After calcination at 500-1200oC, we found the β-Zn2SiO4 appeared in amorphous state around 600oC and the α-Zn2SiO4 appeared in the crystalline state around 700oC. From the experimental data, the te是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
In this approach, we successfully use nucleophilic addition and 2-step hydrolysis for nano-meter sized zinc orthosilicate. After calcination at 500-1200oC, we found the β-Zn2SiO4 appeared in amorphous state around 600oC and the α-Zn2SiO4 appeared in the crystalline state around 700oC. From the experimental data, the te
问题补充： |
|
2013-05-23 12:21:38
在這種方法，我們成功地使用親核加成和2步水解為納米米大小的原矽酸鋅。
|
|
2013-05-23 12:23:18
在這種做法,我們成功地使用nucleophilic除和2-步水解,納米大小orthosilicate鋅。 進後,我們發現在500-1200oc的-zn2sio4 600oc周圍出現在哪一個混亂狀態的-zn2sio4似乎在周圍國家的結晶700。 從實驗數據,溫度較低的階段是轉型的大量系統。
|
|
2013-05-23 12:24:58
在這種方法，我們為毫微米大小的鋅orthosilicate成功地使用親核加成和2步加水分解。 在鍛燒以後在500-1200oC，我們發現了β-Zn2SiO4出現於無定形態在600oC附近，并且α-Zn2SiO4出現於水晶狀態在700oC附近。 從實驗性數據，溫度階段變革是低比較大塊系統。 另外， SEM加上EDX顯示微粒大小是大約50-100毫微米和比率Si ： 鋅： O是1 ： 3: 5，歸因於計數X-射線從ZnO副產物。 這研究對新穎的綜合性路線和對鋅orthosilicate nanocrystals的階段變革的理解貢獻。
|
|
2013-05-23 12:26:38
在此方法中，我們成功地使用親核加成和 2 步水解為矽酸鋅納米大小。在 500-1200c 的煆燒後, 我們發現 β-Zn2SiO4 出現在 600oC 周圍的無定形狀態和 α Zn2SiO4 出現在 700oC 周圍的結晶狀態。從實驗資料看，相轉變較低的溫度相比大容量系統。此外，加上 EDX 的掃描電鏡顯示顆粒大小是周圍 50-100 nm 和矽比： 鋅： O 是 1： 3： 5，歸因於 x 射線計數從氧化鋅的副產品。這項研究為新型的合成路線和鋅矽酸納米晶相變的理解作出了貢獻。
|
|