求翻译：The IR spectrum of the compound K2AlTi(PO4)3 is shown in Fig. 5. To assign the IR peaks to vibrational modes, we examine the modes and frequencies observed in similar compounds. The broad and intense absorption bands appearing at 1274, 1150, 1007cm−1are characteristic of P O stretching vibration in the PO 4 tetrahedron是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The IR spectrum of the compound K2AlTi(PO4)3 is shown in Fig. 5. To assign the IR peaks to vibrational modes, we examine the modes and frequencies observed in similar compounds. The broad and intense absorption bands appearing at 1274, 1150, 1007cm−1are characteristic of P O stretching vibration in the PO 4 tetrahedron
问题补充： |
|
2013-05-23 12:21:38
化合物K2AlTi （PO 4） 3的IR光谱示于图。
|
|
2013-05-23 12:23:18
红外频谱的复合K2alti(PO4)3图所示。 5。 要指派IR山峰振动模式,我们研究的模式和频率中观察到相似的化合物。 广泛的吸收带,紧张出现在1274、1150、1007CM-1的特点是拉伸P O中的振动PO4四面体,带组650-550CM-1是弯曲振动的埔债券,在479CM-1是由于X O(X=AL、TI)振动。
|
|
2013-05-23 12:24:58
复合K2AlTi PO4 3的(红外光谱)显示在。 5. 要分配IR峰顶到振动方式，我们审查被观察的方式和频率在相似的化合物。 出现于1274年1150年， 1007cm−1are的宽广和强烈的吸收带宽舒展振动在PO 4四面体的典型P O，带小组在650-550cm −1弯曲PO债券的振动，并且带在479cm −1归结于X O (X=Al，钛) 振动。 紫外力吸收光谱K2AlTi( PO4) 3取决于散射测量。 如所显示。 6，强的吸收峰在220nm前后出现。
|
|
2013-05-23 12:26:38
红外光谱的复合 K2AlTi (PO4) 3 如图 5 所示。要分配到的振动模式的红外光谱峰，我们检查的方式和在类似化合物中观察到的频率。广泛和强烈吸收带出现在 1274年，1150，1007cm−1are 特征的 P O 伸缩振动在大埔 4 四面体，带组在 650 — — 550 厘米 − 1 弯曲振动的大埔债券和乐队在 479 厘米 − 1 是由于 X O (X = Al，Ti) 振动。紫外-可见吸收光谱的 K2AlTi (PO4) 3 由漫反射测量。如图 6 所示，所以周围 220nm 的强吸收峰出现在。
|
|
2013-05-23 12:28:18