求翻译：Fig. 5 shows the dependence of the remanence ratio and coercivity of films on the film thickness. From Fig.5, it can be seen that the remanence ratio increased drastically from d=22.5nm to d=45 nm, then nearly linearly decreases from the peak value of mr to 0.71 with the increase of film thickness. The higher remanence是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Fig. 5 shows the dependence of the remanence ratio and coercivity of films on the film thickness. From Fig.5, it can be seen that the remanence ratio increased drastically from d=22.5nm to d=45 nm, then nearly linearly decreases from the peak value of mr to 0.71 with the increase of film thickness. The higher remanence
问题补充： |
|
2013-05-23 12:21:38
图。
|
|
2013-05-23 12:23:18
图。 5所示的依赖剩磁比率和矫顽力的电影胶片厚度。 从5,可以看出,剩磁比率大幅增加从D=22纳米制程,D=45纳米制程,然后几乎呈线性上升下降的高峰值0.71涂议员的薄膜厚度的增加。 高的剩磁比率表明,此处显示的磁性颗粒在fepd合金膜交流耦合。 一个最大值=0.79,对D=45纳米制程。
|
|
2013-05-23 12:24:58
。 5个展示影片remanence比率和矫顽性的依赖性对胶片厚度。 从，它能被看见remanence比率从d=22.5nm猛烈地增加了到d=45 nm，然后从先生的最大值几乎线性地减少到0.71随着胶片厚度的增加。 这里显示的更高的remanence比率建议磁性粒子在FePd合金影片交换被结合。 mr=0.79最大价值为d= 45毫微米获得。 根据模型Kneller和Ha假发(11)，适当的粒度在FCT阶段可能提高交换联结。 影片Hc从20迅速地增加到3200Oe，然后价值被减少对2800Oe。 矫顽性和各向异性现象常数之间的关系可以被表达如下：
|
|
2013-05-23 12:26:38
图 5 显示的剩磁比依赖和矫顽力的电影上膜厚度。从图 5，可以看出剩磁比大幅增至 d = 22.5nm d = 45 毫微米，然后几乎呈线性减小峰值的先生从到 0.71 与薄膜厚度的增加。此处所示的剩磁比表明，在 FePd 合金薄膜的磁性粒子交换耦合。先生最大值 = 0.79 得到 d = 45 毫微米。根据模型内勒和医管局-假发 [11]，FCT 相适当的晶粒尺寸可以提高交换耦合。Hc 的电影从 20 迅速增加到 3200Oe，然后值下降至 2800Oe。矫顽力和各向异性常数之间的关系可以表示为:
|
|
2013-05-23 12:28:18