求翻译：When metal materials are subjected to tensile stress in the corrosive medium, the corrosion rate will increase because of the synergistic effect related to the corrosive medium and tensile stress. This phenomenon is called stress corrosion. Stress corrosion is not only a simple superposition of environment and stress, 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
When metal materials are subjected to tensile stress in the corrosive medium, the corrosion rate will increase because of the synergistic effect related to the corrosive medium and tensile stress. This phenomenon is called stress corrosion. Stress corrosion is not only a simple superposition of environment and stress,
问题补充： |
|
2013-05-23 12:21:38
正在翻译，请等待...
|
|
2013-05-23 12:23:18
当金属材料受到拉伸应力腐蚀介质中,腐蚀速度会增加,因为相关的协同作用的腐蚀介质,拉伸应力。 这种现象被称为应力腐蚀。 应力腐蚀不仅是一个简单叠加的环境和压力,同时也面临着越来越复杂的现象。 即使在拉伸应力远远低于屈服强度,也会使金属的脆化断裂后材料的时间。
|
|
2013-05-23 12:24:58
当金属材料在腐蚀性媒介被服从到张应力，腐蚀速率将增加由于协合效应与腐蚀性媒介和张应力有关。 这种现象称应力腐蚀。 应力腐蚀是环境和重音的不仅简单的叠置，而且一种更加复杂的现象。 即使张应力低于出产量，它在时期以后也将导致金属材料脆性断裂。 应力腐蚀造成的金属破裂没有症状，经常导致主要事故。 所以，应力腐蚀是最破坏性和最有害一个在腐蚀的所有类型
|
|
2013-05-23 12:26:38
当金属材料受到拉伸应力腐蚀性介质中时，腐蚀速率会增加由于涉及的腐蚀性的介质和拉伸应力的协同作用。这种现象称为应力腐蚀。应力腐蚀不是只简单叠加的环境和压力，但也是一个更复杂的现象。即使拉伸应力是远低于屈服强度，它也会使后一段时间的金属材料的脆性断裂。应力腐蚀引起的金属断裂有无症状，往往导致重大事故。因此，应力腐蚀是腐蚀的目前最具破坏性和有害在所有类型
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区