求翻译：We target to reflect the wavelengths from 700–1100 nm which is the heat-producing region of the infrared radiations, and the irradiance intensity starts to diminish at the wavelengths longer than 1100 nm. Thus for an effective reflection of thermal infrared light, particle size should be around 350–550 nm. In the previ是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
We target to reflect the wavelengths from 700–1100 nm which is the heat-producing region of the infrared radiations, and the irradiance intensity starts to diminish at the wavelengths longer than 1100 nm. Thus for an effective reflection of thermal infrared light, particle size should be around 350–550 nm. In the previ
问题补充： |
|
2013-05-23 12:21:38
null
|
|
2013-05-23 12:23:18
我们的目标反映的波长从 700 - 1100 nm 的发热区域的红外辐射和辐照度的强度开始减少在波长大于 1100 nm 的。 从而有效的反映了热红外光、粒子大小应在 350 - 550 nm 。 在前面几节中的结果表明 , 热处理有利于增长的颗粒大小 ( d ) , 这提高了反射率的二氧化钛。
|
|
2013-05-23 12:24:58
我们瞄准反射波长从是红外辐射的热生产的区域的700-1100毫微米，并且irradiance强度开始长期减少在波长比1100毫微米。 因而为热量红外线的有效的反射，微粒大小应该是大约350-550毫微米。 在前面的部分，结果表示，热治疗在微粒大小d倾向 (成长)，增加TiO2反射率。 贬低的反射率效率开始，当温度到达990 1C (为4 h， d ¼ 563毫微米由DLS) 和二个其他更加严厉的条件，由于微粒直径的偏差从最宜的大小 (350-550毫微米) 为反射heat-generating波长。 这在中间红外区域也解释C1000-2和C1000-4更高的反射率，显示在补充情况。 由于他们的
|
|
2013-05-23 12:26:38
我们的目标反映从 700-1100 nm 的是热产区的红外辐射波长和辐照强度开始减少在波长长于 1100 nm。因此对于热红外灯有效反射，粒子大小应周围 350-550 毫微米。在前面的章节中，结果表明热处理有利于增长，粒径 (d)，这增加了 TiO2 的反射率。反射效率开始降解当温度达到 990 1 (4 小时，在那里由 DLS d¼563 nm) 和两个其他更严格的条件，从优化反映热量产生波长的大小 (350-550 nm) 粒径的偏差。这也解释了 C1000-2 和 C1000-4 在中红外波段，补充资料所示的高反射率。由于其较大的粒子大小 (571 nm 和 618 毫微米)，菲涅耳的
|
|