求翻译：The 0.2-0.3 mm thick cold-rolled sheets and annealed sheets of high silicon steel were produced by rolling process, then punching tests were carried out at room temperature to 150 ℃. The punchability and punching fracture behavior were investigated by means of scanning electron microscope (SEM) and electron back-scatte是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The 0.2-0.3 mm thick cold-rolled sheets and annealed sheets of high silicon steel were produced by rolling process, then punching tests were carried out at room temperature to 150 ℃. The punchability and punching fracture behavior were investigated by means of scanning electron microscope (SEM) and electron back-scatte
问题补充： |
|
2013-05-23 12:21:38
null
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
0.2-0.3毫米厚实的被冷轧的板料和高硅钢锻炼的板料是通过滚动过程生产的，然后猛击的测试被执行了在室温对150 ℃。 punchability和猛击的破裂行为通过扫描电子显微镜SEM (被调查了) ，并且电子驱散了衍射 (EBSD)。 它被发现高硅钢展示好punchability被冷轧的板料在0.01毫米的情况下拳打死清除和在温度100 ℃; 锻炼的板料的punchability以微粒的大小比那好锻炼的板料以粗糙的粒度; 猛击的温度150 ℃为锻炼的高硅钢片是适当的特别是以粗糙的粒度由于猛击的边缘质量。 锻炼的高硅钢片主要分裂飞机是 () 脆性断裂发生在低温的100个晶体学平面。 分裂系统包
|
|
2013-05-23 12:26:38
0.2-0.3 毫米厚的冷轧薄板及高硅钢退火的片，制得轧制过程，然后在室温至 150 ℃ 进行冲压试验。加工和冲压断裂行为进行了扫描电子显微镜 (SEM) 和电子背散射衍射 (EBSD)。它是发现高硅钢冷轧显示良好的加工条件下的 0.01 毫米冲压模具间隙，在温度为 100 ℃;退火板料与细晶粒尺寸的加工是优于退火板的晶粒粗大;冲孔温度 150 ℃ 适于高硅钢退火的板尤其是由于冲孔边缘质量粒度较粗。高硅钢退火的板主要的解理面是 {100} 晶面，在低的温度下发生脆性断裂。乳沟系统包括 {100} 110 和 {100} 100，和由一个或两个他们完成解理断裂。高硅钢薄钢板的加工与冲孔温度、 晶
|
|