求翻译：For conventional shear test, because of low speed limitations, the dominant failure mode tends to be solder itself, and the brittle fracture at the interface is quite scarce. This means the traditional shear test is difficult to compare the effects of different pad surface finishes, solder alloys, microstructures, and 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
For conventional shear test, because of low speed limitations, the dominant failure mode tends to be solder itself, and the brittle fracture at the interface is quite scarce. This means the traditional shear test is difficult to compare the effects of different pad surface finishes, solder alloys, microstructures, and
问题补充： |
|
2013-05-23 12:21:38
对于传统的剪切试验，因为低转速的限制，主要的故障模式往往是焊料本身，并在界面的脆性断裂是相当匮乏。这意味着传统的剪切试验是难以比较不同焊盘表面处理，焊料合金的微观结构，以及法团校董会的影响，界面附近
|
|
2013-05-23 12:23:18
为常规剪试验,因为低速度的限制,这主要故障模式往往是焊锡本身,和脆弱骨折的界面上是相当少。 这意味着传统剪试验的影响是很难比较不同垫表面装饰,焊锡合金、微结构,和法团校董会的附近接口
|
|
2013-05-23 12:24:58
为常规剪测试，由于低速局限，统治失败形式倾向于是焊剂，并且脆性断裂在接口是相当缺乏的。 这意味着传统剪测试是难在接口附近比较不同的垫表面结束、焊剂合金、微结构和IMCs的作用
|
|
2013-05-23 12:26:38
常规剪切试验，由于的低速度限制，占主导地位的失效模式往往是焊锡本身，和脆性断裂的接口是相当少。这意味着传统剪切试验很难比较不同垫表面光洁度的影响，界面附近焊料合金、 微观结构和内部管理咨询处
|
|
2013-05-23 12:28:18
常规剪切试验，由于的低速度限制，占主导地位的失效模式往往是焊锡本身，和脆性断裂的接口是相当少。这意味着传统剪切试验很难比较不同垫表面光洁度的影响，界面附近焊料合金、 微观结构和内部管理咨询处
|