求翻译：Consider the forms and structure of excess ferrite in hypoeutectoid steels. The ferrite is found in two forms: compact equiaxial grains and oriented Widmannstatten plates (Figure 3.7). Compact precipitates of hypoeutectoid ferrite appear predominantly at austenite grain boundaries, whereas Widmannstatten plates are for是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Consider the forms and structure of excess ferrite in hypoeutectoid steels. The ferrite is found in two forms: compact equiaxial grains and oriented Widmannstatten plates (Figure 3.7). Compact precipitates of hypoeutectoid ferrite appear predominantly at austenite grain boundaries, whereas Widmannstatten plates are for
问题补充： |
|
2013-05-23 12:21:38
考虑亚共析钢中过剩的铁素体的形式和结构。铁素体是有两种形式：紧凑型等轴晶粒和面向Widmannstatten板（图3.7）。紧凑型亚共析铁素体析出主要出现在奥氏体晶界，而Widmannstatten板内粒形成。 Widmannstatten铁氧体是观察，只有在与C和小于0.4％，而粗粮奥氏体钢。由于奥氏体晶粒尺寸的减少，铁素体的形成等轴grainsgrows份额。 Widmannstatten铁氧体形成了从A3（50℃或90℉）温度区间为600至550℃（1112年至1022年℉）。与中钢的碳含量的增加，Widmannstatten铁氧体结构中的份额降低。
|
|
2013-05-23 12:23:18
考虑的形式和结构过剩的铁氧体在hypoeutectoid钢。 铁氧体的发现是在两种形式:契约equiaxial谷物和面向widmannstatten板(图3.7)。 协约的沉淀物hypoeutectoid铁氧体似乎主要是在奥氏体粮食界线,而widmannstatten板内形成谷物。 观察到的widmannstatten铁氧体是只有在钢材,少於0.4%C和而不是粗粮的奥氏体。
|
|
2013-05-23 12:24:58
正在翻译，请等待...
|
|
2013-05-23 12:26:38
考虑的形式和结构过剩铁氧体共析钢。铁素体发现两种形式： 压缩正等轴测图谷物和面向魏氏板 （图 3.7）。紧凑的亚共析度铁氧体沉淀主要出现在奥氏体晶粒间界，而魏氏板内颗粒形成。魏氏铁氧体只跌幅小于 0.4 %c，而是粗粮的奥氏体钢。奥氏体的尺寸谷物减少，在窗体正等轴测图 grainsgrows 铁氧体的份额。魏氏铁素体的形成需要来自 A3 的温度间隔 （50℃or 90℉） 到 600 至 550 ℃ （1112–1022℉）。钢的碳含量增加，降低了魏氏铁氧体结构中的份额。
|
|