求翻译:户外硬聚氯乙烯门窗用型材的加热后尺寸变化率按试验标准ASTM D 1042的规定[82℃(180°F)、水浴、30min]进行检测。当型材的壁厚>1.02mm(0.040in)时,所有被测量表面的加热后尺寸变化率的平均值≤2.2%,最大值≤2.4%;当型材的壁厚≤1.02mm(0.040in)时,所有被测量表面的加热后尺寸变化率的平均值≤3.0%。是什么意思?![]() ![]() 户外硬聚氯乙烯门窗用型材的加热后尺寸变化率按试验标准ASTM D 1042的规定[82℃(180°F)、水浴、30min]进行检测。当型材的壁厚>1.02mm(0.040in)时,所有被测量表面的加热后尺寸变化率的平均值≤2.2%,最大值≤2.4%;当型材的壁厚≤1.02mm(0.040in)时,所有被测量表面的加热后尺寸变化率的平均值≤3.0%。
问题补充: |
|
2013-05-23 12:21:38
Outdoor hard PVC doors and windows of the size profile of the heating rate of change with test standard astm d 1042 [82 ° C (180 ° f), water bath, 30min] were detected. When the profile of the wall thickness> 1.02mm (0.040in), all the heating of the surface to be measured after the dimensional ch
|
|
2013-05-23 12:23:18
Outdoor hard PVC doors and windows with the heated material size rate of change on the basis of the 1042 standard ASTM D [ 82 °C F (180 °) and Jacuzzi as well as 30 min], to conduct the test. When in the profile of the wall thickness >1.02 MM (0.040 in) all the measurement of surface heating, the
|
|
2013-05-23 12:24:58
The outdoors hard polyvinyl-chloride windows and doors after the molding heating the size rate of change according to experimental standard ASTM the D 1042 stipulations (82℃(180°F), the water bath, 30min) carry on the examination.When molding wall thickness >1.02mm(0.040in), after possesses is su
|
|
2013-05-23 12:26:38
Heated outdoor PVC door and window profiles the size change rate required by the test standard ASTM d 1042 [82 ° c (180 ° f), water baths, 30min] for testing. When the profile thickness of >1.02mm (0.040in), all of average size change rate after the measurement of surface heating ≤ 2.2%, maximum
|
|