求翻译：Electrochemical measurements have shown that low-manganese (∼0.2% Mn) stainless steels with low (⩽1.2% Mo) or no molybdenum exhibit a higher pitting resistance in neutral sodium chloride (0.005–2 M) than the analogous commercial steels containing 1.4 ∼ 2% Mn and ∼2.8% Mo, or the special laboratory heats of similar comp是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Electrochemical measurements have shown that low-manganese (∼0.2% Mn) stainless steels with low (⩽1.2% Mo) or no molybdenum exhibit a higher pitting resistance in neutral sodium chloride (0.005–2 M) than the analogous commercial steels containing 1.4 ∼ 2% Mn and ∼2.8% Mo, or the special laboratory heats of similar comp
问题补充： |
|
2013-05-23 12:21:38
电化学测量表明，低锰（〜0.2％Mn的）与不锈钢低（⩽1.2％MO）或无钼展览中性氯化钠较高的耐点蚀（0.005-2男）比类似的商业钢含有1.4〜 2％Mn和〜2.8％钼，或特殊的实验室加热类似的成分，但高含量，〜0.2％。显微镜检查，X射线探针分析和SAM调查揭示了钢的耐点蚀性能，非金属夹杂物的组成，并在夹杂物和邻接矩阵所形成的钝化膜的组成之间的相关性。在酸性和中性硫酸盐的电化学测量表明，低锰钢一般具有较高的能力比商业的钝化。相比之下在中立的解决方案，也是在那些包含氯化物的行为，修改后的既不武，也不钛钢的被动是不太稳定，在酸性介质中比其他小说钢。
|
|
2013-05-23 12:23:18
(形) 电气化学的
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
电化学测量表明，低 （⩽1.2%钼） 或没有钼低锰 (∼0.2%锰) 不
|
|
2013-05-23 12:28:18
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区