求翻译：The composition of the oxides formed on 304 stainless steel stress corrosion specimens in high temperature waters have been measured by AES. The compositions of the films varied with water chemistry and temperature and were different for slow strain rate and U-bend specimens. The thickness of the oxide and enhancement 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The composition of the oxides formed on 304 stainless steel stress corrosion specimens in high temperature waters have been measured by AES. The compositions of the films varied with water chemistry and temperature and were different for slow strain rate and U-bend specimens. The thickness of the oxide and enhancement
问题补充： |
|
2013-05-23 12:21:38
304不锈钢应力腐蚀标本在高温水域形成的氧化物的组成已通过AES测量。薄膜的成分与水化学和温度不同，慢应变速率和U型弯曲试样的不同。薄膜铬的氧化物和增强的厚度减少与增加氯在水中。对于U型弯曲试样，抗开裂的影片，但厚的薄膜和高铬含量的铬含量增加薄膜的厚度和增加了阻力较小开裂，慢应变速率试验。
|
|
2013-05-23 12:23:18
成立的组成上氧化物304不锈钢压力腐蚀样本在高温水域已按AES。 该作品的影片的各种与水化学和温度和压力是不同的缓慢速度和u-弯标本。 厚度的氧化物和加强铬的减少在电影与增加的氯化水。
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
304 不锈钢应力腐蚀样品在高温水域上形成的氧化物的组成进行过原子发射光谱法测定。组成的电影随水化学成分和温度，不同的慢应变速率和 u 型标本。氧化和增强的电影中铬的厚度减少了增加水中的氯。U 型的标本，抗开裂增加增加膜厚度与电影但厚膜铬含量高的铬含量给予破解慢应变速率试验的阻
|
|