求翻译：The thickness, chemical composition and microstructure of anodised coatings formed on magnesium alloy AZ91D at various anodising current densities were measured. It was found that all these parameters could be affected by anodising current density, and hence the coatings formed at different anodising current densities 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The thickness, chemical composition and microstructure of anodised coatings formed on magnesium alloy AZ91D at various anodising current densities were measured. It was found that all these parameters could be affected by anodising current density, and hence the coatings formed at different anodising current densities
问题补充： |
|
2013-05-23 12:21:38
各种阳极氧化电流密度在AZ91D镁合金上形成的阳极氧化涂层的厚度，化学成分和微观结构进行了测量。结果发现，所有这些参数可以通过阳极氧化电流密度的影响，因此在不同的阳极氧化电流密度形成的涂料有不同的腐蚀电阻。这表明，如果一个设计适当的电流波形是用阳极氧化，阳极氧化涂层的防腐性能，可改善。此外，实验结果的基础上，一些物理，化学和电化学反应在阳极氧化过程中所涉及的提出来解释本文中的阳极氧化行为。
|
|
2013-05-23 12:23:18
的厚度,机身采用阳极化处理的化学组成和微结构涂料形成鎂合金az.91d在各种anodising电流密度是衡量。 人们发现,所有这些参数可以是受anodising电流密度,因此形成的涂料在不同anodising电流密度有不同耐腐蚀。 这表明,腐蚀涂层机身采用阳极化处理的表现可以改进如果一个设计目前是用于anodising波形。
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
测量厚度、 化学成分及各种阳极电流密度的镁合金 AZ91D 电镀层的微观结构
|
|