求翻译：An AISI 420 (13Cr) martensitic stainless steel was tested in environments containing different amounts of H2S, CO2, Cl− and acidity, at temperatures varying from 22 to 140°C. The sulphide stress corrosion cracking (SSCC) resistance was assessed with three different types of testing methods: uniaxially constant load; co是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
An AISI 420 (13Cr) martensitic stainless steel was tested in environments containing different amounts of H2S, CO2, Cl− and acidity, at temperatures varying from 22 to 140°C. The sulphide stress corrosion cracking (SSCC) resistance was assessed with three different types of testing methods: uniaxially constant load; co
问题补充： |
|
2013-05-23 12:21:38
一个AISI 420（13Cr）马氏体不锈钢在含有不同数量的硫化氢，二氧化碳，氯离子和酸度，温度不同从22到140 ° C。的环境测试评估三种不同类型的测试方法：单向恒定负载;恒应变（U型）和慢应变速率（SSRT）的硫化物应力腐蚀开裂（SSCC）的阻力。高到SSCC的敏感性，这证明在硫化氢环境中，而二氧化碳的增加有抑制作用，由于保护膜的形成。高氯离子浓度和低pH值有不利影响。此外，SSCC的易感性与实际腐蚀速率：高腐蚀速率造成更多的离域的攻击。在这方面，氯，硫化氢和酸化pH值可能会增加腐蚀速率上SSCC的行为与最后的有益作用。 SSRT技术，由于其灵敏度高，表明应力腐蚀开裂的CO2饱和的硫化氢
|
|
2013-05-23 12:23:18
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
|
|
2013-05-23 12:28:18
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区