求翻译：The strong plasmon band observed at 520 nm in the case of Au NPs containing sol has been significantly dampened due to the formation of Pd shells. Grazing incidence X-ray diffraction and transmission electron microscopy(including scanning TEM, EDS using nanoprobe, and HRTEM)analyses revealed the core-shell structure of 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The strong plasmon band observed at 520 nm in the case of Au NPs containing sol has been significantly dampened due to the formation of Pd shells. Grazing incidence X-ray diffraction and transmission electron microscopy(including scanning TEM, EDS using nanoprobe, and HRTEM)analyses revealed the core-shell structure of
问题补充： |
|
2013-05-23 12:21:38
在金奈米粒子含溶胶在520 nm处观察到强烈的等离子体带已大大挫伤由于PD炮弹形成。掠入射X射线衍射和透射电子显微镜（TEM，EDS使用纳米探针，扫描和HRTEM）分析表明，NPS的核 - 壳结构。上述溶胶可用于准备AU @ PD核心壳NPS成立玻璃基板上的氧化铝涂层。金PD NPS转化为内部后热处理电影矩阵金钯合金NPS在500℃空气中。
|
|
2013-05-23 12:23:18
plasmon公司带的强大在520nm的核动力源的非盟案包含sol已经大大减弱由于pd炮弹的形成。 放牧发生x射线衍射和传输电子显微镜(tem包括扫描,使用电子数据系统公司(edsnanoprobe和hrtem)分析揭示了核心的外壳结构的nps。 上述解决方案可用于准备au@pd核心的氧化铝涂层的玻璃外壳核动力源成立为法团承印物。
|
|
2013-05-23 12:24:58
强的胞质基因带被观察在520毫微米在Au包含sol的NPs情况下significantly被挫伤的归结于Pd壳的形成。 吃草发生X-射线衍射和传输电子显微镜术(包括扫描TEM、EDS使用nanoprobe和HRTEM)分析显露了NPs的核心壳结构。 上述sol在玻璃基体可以用于准备Au@Pd核心壳NPs被合并的铝土涂层。 Au@Pd NPs在空气被变换了对AuPd合金NPs在film矩阵里面在热治疗以后在500 °C。
|
|
2013-05-23 12:26:38
正在翻译，请等待...
|
|
2013-05-23 12:28:18
强有力的 plasmon 乐队在控制溶胶的 Au NPs 的情况下在 520 nm 处观察是 signi？cantly 由于 Pd 的构成沮丧壳。放牧发生率的 X 射线衍射和传送电子 microscopy(including scanning TEM, EDS using nanoprobe, and HRTEM) 分析透露 NPs 的核心壳的结构。以上溶胶可能用于在玻璃品上准备 Au@Pd 核心壳 NPs 合并的氧化铝层 substrates。Au@Pd NPs 被转变到 Au-Pd 合金里面的 NPs？lm 矩阵在空气中的 500 ° C 的热度治疗之后。
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区