求翻译：A carbon black of N-220 type (VCB, Korea Carbon Black Co.) was selected as a reinforcement, and the loading level was fixed to be 50 phr. In order to create the polar functional groups on carbon black surfaces, the CBs were immersed in two different solutions of 0.1 N KOH and C6H6 (BCB and NCB, respectively) for 24 h. 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
A carbon black of N-220 type (VCB, Korea Carbon Black Co.) was selected as a reinforcement, and the loading level was fixed to be 50 phr. In order to create the polar functional groups on carbon black surfaces, the CBs were immersed in two different solutions of 0.1 N KOH and C6H6 (BCB and NCB, respectively) for 24 h.
问题补充： |
|
2013-05-23 12:21:38
炭黑的N-220型（VCB，韩国炭黑有限公司。）被选为加固，负荷水平固定为50份。以创建炭黑表面的极性官能团，CBS浸泡24小时0.1 N KOH和C6H6（BCB和NCB），分别在两个不同的解决方案。使用前，后分析，所使用的化学残留物被拆除索氏提取丙酮在80◦C 2 H沸腾。最后，碳黑人用蒸馏水冲洗数次，并在真空烘箱中干燥90◦c为12小时。苯乙烯 - 丁二烯橡胶（SBR-1500，势必苯乙烯：23.5％，顺-1，4：17％，反式-1，4：68％，1,2 - 乙烯：15％，锦湖石化合作的韩国。 ）被选为本研究橡胶。 TBBS
|
|
2013-05-23 12:23:18
一个碳黑色的n-220类型(使用vcb,韩国碳黑公司)被选为一个增援力量,而加载一级是固定,将有50名关心 为了创建的碳黑表面上极功能组,美国哥伦比亚广播公司(cbs就沉浸在两种不同的解决方案0.1nkoh和c6h6(bcb和国家协调机构,分别为24h。 在使用之前经过分析,残留化学品被使用的soxhlet提取用丙酮沸点80◦c2h。
|
|
2013-05-23 12:24:58
正在翻译，请等待...
|
|
2013-05-23 12:26:38
炭黑的 N-220 型 (真空断路器，韩国炭黑有限公司) 被选为一种强化，加载级别被定为 50 心想为了创建在炭黑表面的极地功能组，CBs 就沐浴在两个不同的解决方案，0.1 N KOH 和 C6H6 (BCB 和国家协调机构，分别） 为 24 h.在使用后分析之前，使用的残余化学品粗脂肪删除的丙酮的 80 一道 C 为 2 h 沸腾。最后，汽车 bon 黑人被水洗几次用蒸馏水和 90 一道 C 为 12 h 在真空炉中干燥。Styrene– 丁二烯橡胶 (SBR-1500，绑定苯乙烯： 23.5%，独联体-1，4： 17%、 反式-1，4： 68%，1，2-乙烯： 锦湖石化的 15%。韩国有
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区