求翻译：The LEADCAP additive has a melting point below a normal HMA production temperature and can be added to the asphalt mixture (plant-mixed type process) or to the asphalt binder (pre-mixed type process) allowing for the production and placement of the mixture at about 30 ºC below the temperatures of conventional HMAs. Thi是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The LEADCAP additive has a melting point below a normal HMA production temperature and can be added to the asphalt mixture (plant-mixed type process) or to the asphalt binder (pre-mixed type process) allowing for the production and placement of the mixture at about 30 ºC below the temperatures of conventional HMAs. Thi
问题补充： |
|
2013-05-23 12:21:38
leadcap添加剂有一个正常HMA的生产温度低于熔点，并可以添加到沥青混合料（植物混合型过程）或沥青粘结剂（预混合型过程），使混合物的生产和安置在低于常规HMAS温度约30℃。通常这种添加剂在沥青粘结剂（11）重量1.5％至4.0％的速度增加。
|
|
2013-05-23 12:23:18
leadcap添加剂的熔点低于一个正常的hma生产温度,并可以添加到沥青制成的混合物(植物的混合类型)或与沥青粘结剂(预混合类型过程)允许生产和摆放位置约30ºc混合物的温度下界的传统。 这种添加剂是一般添加在增长率为1.5%至4.0%(按重量计算的沥青粘结剂(11)。
|
|
2013-05-23 12:24:58
LEADCAP添加剂有一个熔点在一个正常HMA生产温度之下，并且可以增加到沥青混合物(植物混杂的类型过程)或到考虑到混合物的生产和安置的沥青结合料(预先混合的类型过程)在大约30 ºC在温度常规HMAs之下。 这个添加剂典型地增加以率的1.5%到4.0%按沥青结合料(11重量计算)。
|
|
2013-05-23 12:26:38
LEADCAP 添加剂已低于正常的沥青混合料生产温度的熔点和沥青混合料 （植物混合类型的过程），或允许生产和下面的常规 HMAs 温度约 30 篊混合放置的沥青 （预混的型过程） 可以添加。这种添加剂通常按重量计的沥青 （11） 将添加在率 1.5%至 4.0%。
|
|
2013-05-23 12:28:18
LEADCAP 添加剂有在一正常的高端内存区生产温度下面的熔点和可以增加了沥青的混合 ( 植物混合的类型过程 ) 或到沥青的 binder( 掺和前类型过程 ) 在大约 30 处考虑到混合的生产和放置温度传统的高端内存区下的 oC。这种添加剂通常被加按重量计按 1.5% 比率到 4.0% 沥青的 binder 中 (11)。
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区