求翻译：The PI coated substrate was firstly placed in a hot oven at 100℃ for 20min to dry the solvent,and then hard-baked at 200℃ for 1h to complete the imidization.After the curing,the PI substrate was uniaxially rubbed with a velvet cloth to induce LC alignment.是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The PI coated substrate was firstly placed in a hot oven at 100℃ for 20min to dry the solvent,and then hard-baked at 200℃ for 1h to complete the imidization.After the curing,the PI substrate was uniaxially rubbed with a velvet cloth to induce LC alignment.
问题补充： |
|
2013-05-23 12:21:38
PI涂布基材首先放置在热炉在100℃20分钟干溶剂，然后在200℃，时间为1h硬烤完成的imidization.after的，固化，PI基板单轴用丝绒布擦诱导LC对齐。
|
|
2013-05-23 12:23:18
pi涂层基材是第一放在一个很热的烤箱在100°℃干燥的溶剂20分钟内即可,然后再硬盘烤在200°℃的1h,完成imidization。在固化之后,与擦uniaxiallypi基材是一个天鹅绒布,以诱使lc对齐。
|
|
2013-05-23 12:24:58
PI被涂上的基体在一个热的烤箱首先安置在100℃为了20min能烘干溶剂， hard-baked在200℃为了1h能然后完成imidization。在治疗以后， PI基体uniaxially摩擦以天鹅绒布料导致LC对准线。
|
|
2013-05-23 12:26:38
PI 涂层基板是首先放置在热炉在 100 ℃ 干燥溶剂，20 分钟，然后烤硬在完成亚胺化 1 h 为 200 ℃。固化后, PI 基板是单轴擦用丝绒布诱使立法会对齐方式。
|
|
2013-05-23 12:28:18
PI 涂上一层的 substrate 首先在 100 处被放到一个热的烤炉中？对于 20 分弄干溶剂，然后努力地烤在 200？1h 若要完成 imidization.After 治好， PI substrate uniaxially 拿着一块光滑的布被摩擦促使 LC 对齐。
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区