求翻译：Thin self-supporting ceramic TiO2-layers with a graded pore structure were prepared by using centrifugal deposition of powders and sols with different particle size distributions from mixed, diluted suspensions. During the evaporation drying step the layers have a strong tendency to warping and crack-formation because 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Thin self-supporting ceramic TiO2-layers with a graded pore structure were prepared by using centrifugal deposition of powders and sols with different particle size distributions from mixed, diluted suspensions. During the evaporation drying step the layers have a strong tendency to warping and crack-formation because
问题补充： |
|
2013-05-23 12:21:38
薄自支持陶瓷氧化钛 2 < INF分级孔结构层，通过使用不同的混合，稀释悬浮颗粒的粒度分布的粉末和溶胶离心沉积准备。在蒸发干燥步骤，层层有一个扭曲的强劲势头和裂纹形成，因为在毛细管压力在上部和底部毛孔造成的差异。四种干燥方法进行了研究，关于为减少或消除毛细管力和生产平面，无裂纹的干标本的适用性。在实验中使用的干燥技术作了简要介绍。应当强调的是，上述层最成功的干燥方法是结合微波干燥和随后的临界点干燥。
|
|
2013-05-23 12:23:18
瘦自支承二氧化钛陶瓷2层孔隙结构与一个分等级的准备使用离心式沉积的粉尘和颗粒大小不同解决方案的分布的混合,稀释后暂停。 在蒸发干燥步骤图层有一种强烈的倾向,变形和裂缝的形成,从而造成不同的毛细血管压力的上限和毛孔的底部。
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
薄自立陶瓷 TiO 2-梯度的孔隙结构的图层都备离心沉积的粉末
|
|
2013-05-23 12:28:18
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区