求翻译：从图2.6可以看出,交联剂用量为0.0013g时,吸水倍数最高达到了387,这是因为交联密度低,水分子容易渗入树脂中使树脂膨胀,进一步亲水而凝胶化,成为高吸水状态是什么意思？

It can be seen from Figure 2.6, when the crosslinker dosage 0.0013g, water up to a multiple of 387, this is because the crosslinking density is low, water molecules easily penetrate the resin, the resin expansion manipulation, and further hydrophilic gel, a high water status

It can be seen from figure 2.6 crosslinking agent, dosage for multiple 0.0013 G, absorb water up to 387, this is because low-density to the Stock Exchange, the water molecules can easily penetrate into resins, the resin swelling further pro-water and gel to become a high-water absorption State

2.6 may see from Figure, when the crosslinking agent amount used is 0.0013g, the absorbing water multiple was highest had achieved 387, this was because the crossing linking density was low, the hydrone easy to permeate in the resin to make the resin to inflate, but further the water affinity the ge

You can see from Figure 2.6, Crosslinking agent dosage for 0.0013g, the water absorption times up to 387, this is because the Crosslinking density is low, water molecules easily infiltrate resin resin swelling, further hydrophilic gel-forming, high water absorption

It can be seen from Figure 2.6, when the crosslinker dosage 0.0013g, water up to a multiple of 387, this is because the crosslinking density is low, water molecules easily penetrate the resin, the resin expansion manipulation, and further hydrophilic gel, a high water status